Boron nitride filled PTFE
View Patent ↗A composition is provided that, in one aspect, may be used in the production of sealing materials, such as gaskets. The composition includes a polytetraflouroethylene matrix and a Boron Nitride filler. In one aspect, the Boron Nitride filler may be provided as a hexagonal, close-packed, Boron Nitride filler that is homogeneously dispersed within the polytetraflouroethylene matrix. In at least one embodiment, the composition is formed by combining quantities of polytetraflouroethylene, Boron Nitride filler, hydrocarbon liquid, and solvent. The liquid and solvent may be removed through various processes prior to sintering the composition to form a full-density, Boron Nitride filled, polytetraflouroethylene matrix that exhibits improved sealability, greater resistance to permeation, and less color contamination.
1. A process for making polytetraflouroethylene matrix-based material, the process consisting essentially of:
combining polytetraflouroethylene particulate and a hydrocarbon liquid to form a polytetraflouroethylene resin;
mixing Boron Nitride filler with the polytetraflouroethylene resin and a solvent to form a slurry; and
removing at least a portion of the hydrocarbon liquid from the polytetraflouroethylene resin to form a cake.
2. The process of claim 1 wherein said solvent is comprised of a light hydrocarbon solvent.
3. The process of claim 1 wherein the removal of at least a portion of the hydrocarbon liquid is at least partially accomplished through filtration.
4. The process of claim 1 further comprising:
calendaring the cake to form a biaxially oriented sheet of material.
5. The process of claim 4 further comprising:
pressing the sheet of material into a pre-formed structure; and
fibrillating the pre-formed structure to form sheets.
6. The process of claim 4 wherein at least a portion of the hydrocarbon liquid is left in the polytetraflouroethylene resin that lubricates and orients particles of the polytetraflouroethylene resin and Boron Nitride as the cake is calendared.
7. The process of claim 4 further comprising:
drying the sheet of material to substantially remove a substantial portion of any remaining hydrocarbon liquid.
8. The process of claim 7 further comprising:
sintering the sheet to form a full-density polytetraflouroethylene matrix containing homogeneously dispersed hexagonal close packed Boron Nitride filler.
9. The process of claim 8 wherein said Boron Nitride filler comprises about 20 percent by weight of the Boron Nitride filled polytetraflouroethylene sheet.