Method of making green-emitting borate phosphors
View Patent ↗There is described a method for the preparation of a green-emitting terbium and cerium co-activated gadolinium magnesium pentaborate phosphor that utilizes a hydrated magnesium hexaborate as a boron source. The hydrated magnesium hexaborate preferably may be represented by the formula MgB 6 O 10 .XH 2 O where X is from 4 to 6, preferably 4.8 to 5.5, and more preferably about 5. The hydrated magnesium hexaborate is combined with oxides of Gd, Ce, and Tb, and at least one magnesium compound selected from MgCl 2 , MgF 2 , and MgO, and then fired in a slightly reducing atmosphere to form the phosphor. The method results in a greater homogeneity of the fired cake and subsequently a higher brightness. In addition, the method preferably requires only one firing step and provides very little or no sticking of the fired cake to the firing boats.
1. A method of producing a green-emitting terbium and cerium co-activated gadolinium magnesium pentaborate phosphor comprising:
(a) combining a hydrated magnesium hexaborate with oxides of Gd, Ce, and Tb, and at least one magnesium compound selected from MgCl 2 , MgF 2 and MgO to form a mixture; and
(b) firing the mixture in a slightly reducing atmosphere to form the phosphor.
2. The method of claim 1 wherein the hydrated magnesium hexaborate has a formula MgB 6 O 10 .XH 2 O, where X is from 4 to 6.
3. The method of claim 2 wherein X is 4.8 to 5.5.
4. The method of claim 2 wherein X is about 5.
5. The method of claim 1 wherein the phosphor has a formula (Gd 1-x-y Ce x Tb y )MgB 5 O 10 , where x has a value from 0.02 to 0.80 and y has a value from 0.01 to 0.40, and x+y<1.
6. The method of claim 5 wherein x has a value from 0.1 to 0.4 and y has a value from 0.02 to 0.2.
7. The method of claim 1 wherein the mixture is fired at a temperature from about 1020° C. to about 1060° C. in a 99% N 2 /1% H 2 atmosphere.
8. The method of claim 1 wherein the hydrated magnesium hexaborate is formed by dissolving boric acid in water to form a boric acid solution, heating the boric acid solution to a temperature of about 90° C., adding magnesium carbonate to the boric acid solution, reducing the temperature of the boric acid solution to within a lower temperature range of from about 35° C. to about 70° C., and maintaining the solution within the lower temperature range for at least about one hour.
9. The method of claim 8 wherein the boric acid solution contains about 6.0 to about 12.0 millimoles of boric acid per 1.0 milliliter of water and about 1.0 to about 2.0 millimoles of magnesium carbonate per 1.0 milliliter water is added.
10. The method of claim 8 wherein the boric acid solution contains about 9.0 to about 10.0 millimoles of boric acid per 1.0 milliliter of water and about 1.5 to about 1.67 millimoles of magnesium carbonate per 1.0 milliliter water is added.
11. The method of claim 9 wherein the molar ratio of H 3 BO 3 to MgCO 3 is 5.75 to 6.25.
12. The method of claim 9 wherein the molar ratio of H 3 BO 3 to MgCO 3 is about 6.0.
13. The method of claim 1 wherein the at least one magnesium compound is selected from MgCl 2 and MgF 2 .
14. A method of producing a green-emitting (Gd 1-x-y Ce x Tb y )MgB 5 O 10 phosphor, wherein x has a value from 0.02 to 0.80 and y has a value from 0.01 to 0.40, and x+y<1, the method comprising:
(a) combining a hydrated magnesium hexaborate with oxides of Gd, Ce, and Tb, and at least one magnesium compound selected from MgCl 2 , MgF 2 and MgO to form a mixture, the hydrated magnesium hexaborate having a formula MgB 6 O 10 .XH 2 O where X is from 4 to 6; and
(b) firing the mixture at a temperature from about 1020° C. to about 1060° C. in a slightly reducing atmosphere to form the phosphor.
15. The method of claim 14 wherein x has a value from 0.1 to 0.4 and y has a value from 0.02 to 0.2.
16. The method of claim 14 wherein the hydrated magnesium hexaborate is formed by dissolving boric acid in water to form a boric acid solution, heating the boric acid solution to a temperature of about 90° C., adding magnesium carbonate to the boric acid solution, reducing the temperature of the boric acid solution to within a lower temperature range of from about 35° C. to about 70° C., and maintaining the solution within the lower temperature range for at least about one hour.
17. The method of claim 16 wherein the boric acid solution contains about 6.0 to about 12.0 millimoles of boric acid per 1.0 milliliter of water and about 1.0 to about 2.0 millimoles of magnesium carbonate per 1.0 milliliter water is added.
18. The method of claim 16 wherein the boric acid solution contains about 9.0 to about 10.0 millimoles of boric acid per 1.0 milliliter of water and about 1.5 to about 1.67 millimoles of magnesium carbonate per 1.0 milliliter water is added.
19. The method of claim 17 wherein the molar ratio of H 3 BO 3 to MgCO 3 is 5.75 to 6.25.
20. The method of claim 14 wherein X is 4.8 to 5.5.
21. The method of claim 14 wherein X is about 5.
22. The method of claim 19 wherein X is 4.8 to 5.5.
23. The method of claim 19 wherein X is about 5.