Superalloy component welding at ambient temperature
View Patent ↗A method for welding superalloy components at ambient temperature conditions while reducing the propensity of the superalloy material to crack as a result of the weld. A root pass region of the weld is formed using a filler material that exhibits ductility that is higher than that of the base superalloy material. The ductile material mitigates stress in the root region, thereby preventing the formation of cracks. A remaining portion of the weld is formed using a filler material that essentially matches the base superalloy material. The method may utilize a pre-weld heat treatment to grow a gamma prime precipitate phase in the superalloy material, a chill fixture to remove heat during welding, a relief cut to reduce stress in the root region, and a conventional post-weld heat treatment.
1. A method of welding to a component formed of a nickel-based precipitation strengthened superalloy material, the method comprising:
heat-treating the component to grow a gamma prime precipitate phase in the superalloy material to a volume percentage of 40-55%;
welding a root portion of a structural weld to the component at ambient temperature while removing heat from the component via a chill fixture by using a root portion filler material exhibiting a ductility greater than a ductility of the superalloy material;
completing the structural weld at ambient temperature while removing heat from the component via the chill fixture by using a structural filler material exhibiting a strength greater than and a ductility less than that of the root portion filler material; and
post-weld heat-treating the component.
2. The method according to claim 1 , wherein the superalloy material comprises one of the group of CM-247LC, IN738, CM247, Rene 80, GTD111, Rene 125, Rene 142, Rene N5, SC180, CMSX-2, CMSX-4, CMSX-10, PWA 1480 and PWA 1484 alloys, the root portion filler material comprises one of the group of Hastelloy W, IN625, Rene 41, Haynes 282 alloys, and the structural filler material comprises one of the group of MarM247, IN738, IN939, and Rene80 alloys.
3. The method according to claim 1 , wherein the root portion of the weld formed with the root portion filler material comprises a root pass only.
4. The method according to claim 1 , wherein the root portion of the weld formed with the root portion filler material comprises at least a root pass only and up to 25% of a total weld thickness.
5. A method of welding to a superalloy material wherein the improvement comprises:
forming a root portion of a structural weld to a superalloy material using a filler material exhibiting a ductility greater than a ductility of the superalloy material; and
forming a remaining portion of the structural weld using a filler material exhibiting a strength greater than and a ductility less than that of the root portion filler material;
wherein the improvement further comprises heat treating the superalloy material prior to forming the root portion of the weld to grow a gamma prime precipitate phase in the superalloy material to a desired volume percentage.
6. The method of claim 5 , wherein the improvement further comprises heat treating the superalloy material prior to forming the root portion of the weld to grow the gamma prime precipitate phase in the superalloy material to a volume percentage of 40-55%.
7. The method according to claim 5 , wherein the root portion of the structural weld formed with the root portion filler material comprises a root pass only.
8. The method according to claim 5 as applied to a nickel based precipitation strengthened superalloy material, and further comprising:
forming the root portion of the structural weld using a solid solution strengthened alloy filler material; and
forming the remaining portion of the structural weld using a precipitation strengthened alloy filler material.
9. The method according to claim 5 as applied to a nickel based precipitation strengthened superalloy material, and further comprising:
forming the root portion of the structural weld using a precipitation strengthened alloy filler material exhibiting a ductility greater than the ductility of the superalloy material; and
forming the remaining portion of the structural weld using a precipitation strengthened alloy filler material essentially matching the superalloy material.
10. The method according to claim 5 , wherein the root portion of the structural weld formed with the root portion filler material comprises at least a root pass only and up to 25% of a total weld thickness.