Oral care layer and related method of manufacture
View Patent ↗An oral care composition including a hydrophilic, aliphatic, polyether-based thermoplastic polyurethane, a glycol polymer, and a poly(N-vinyl lactam). These components form a tacky film having a thickness of about 1 mils to about 50 mils. A whitening agent, such as a peroxide, can be absorbed into the tacky film, and adapted to desorb from the tacky film to whiten teeth to which the film is joined. A method is also provided in which the components are extruded through a twin screw extruder and output to a die to produce the film. The whitening agent can be deposited on the film and absorbed by the film to form a relatively stable oral care composition including the whitening agent.
1. An oral care composition comprising:
a hydrophilic, aliphatic, polyether-based thermoplastic polyurethane material, present in an amount of about 1% to about 25% by weight of the composition,
a hydrophilic polymer present in an amount of about 40% to about 80% by weight of the composition; and
at least one of a glycol polymer and glycerine present in an amount of about 10% to about 40% by weight of the composition,
wherein the thermoplastic polyurethane material, the hydrophilic polymer and the at least one of a glycol polymer and glycerine are mixed together in a mixture to form a hydrogel film layer, the hydrogel included in a film layer having a thickness of about 1 mil to about 50 mils,
wherein the hydrogel film layer including the thermoplastic polyurethane material, the hydrophilic polymer and the at least one of a glycol polymer and glycerine is joined with a substrate layer,
wherein the substrate layer is adapted to wrap a plurality of teeth of a user so as to bring the hydrogel film layer into contact with the teeth,
wherein the hydrophilic, aliphatic, polyether-based thermoplastic polyurethane material becomes tacky when hydrated to promote adhesion of the hydrogel film layer to the teeth when the hydrogel film layer contacts a moist surface of the teeth.
2. The oral care composition of claim 1 wherein the film is formed by extruding the thermoplastic polyurethane material, the hydrophilic polymer and the at least one of a glycol polymer and glycerine through a twin screw extruder.
3. The oral care composition of claim 1 wherein the substrate layer is constructed from wax to form a wax substrate layer.
4. The oral care composition of claim 1 wherein the hydrogel film layer is joined with a structural portion to form a laminate.
5. The oral care composition of claim 3 wherein the at least one of a glycol polymer and glycerine is glycol polymer and the glycol polymer is polyethylene glycol present in an amount of about 30% by weight of the film.
6. The oral care composition of claim 4 wherein the hydrophilic polymer is polyvinyl pyrrolidone present in an amount of about 58% by weight of the film.
7. The oral care composition of claim 1 comprising a water-soluble oral care agent absorbed in the film.
8. The oral care composition of claim 7 wherein the water-soluble oral care agent is a whitening agent which is hydrogen peroxide.
9. The oral care composition of claim 1 comprising at least one of flavorants, sweeteners, colorants, preservatives, and stabilizers.
10. The oral care composition of claim 1 comprising an the oral care agent that is at least one of fluorides, phosphates, stannates, nitrates and peroxides.
11. An oral care composition comprising:
a hydrophilic, aliphatic, polyether-based thermoplastic polyurethane material having a hardness of Shore 60D when dry, and an equilibrium water content of about 500% to about 900%, based on weight of dry thermoplastic polyurethane material;
a glycol polymer; and
a poly(N-vinyl lactam), wherein the glycol polymer is hydrogen bonded to the a poly(N-vinyl lactam);
wherein the hydrophilic, aliphatic polyether-based thermoplastic polyurethane material, the glycol polymer, and the poly(N-vinyl lactam) are mixed together to form a hydrogel film layer having a thickness of about 1 mil to about 50 mils,
wherein the hydrogel film layer including the thermoplastic polyurethane material, the hydrophilic polymer and the glycol polymer is joined with a substrate layer,
wherein the substrate layer is adapted to wrap a plurality of teeth of a user so as to bring the hydrogel film into contact with the teeth,
wherein a peroxide is absorbed into the hydrogel film layer to form a loaded hydrogel film layer, but adapted to desorb from the loaded hydrogel film layer onto a surface of a user's teeth on which the loaded hydrogel film layer is placed by the user to impart a whitening effect on the teeth.
12. The oral care composition of claim 11 wherein the glycol polymer is polyethylene glycol present in an amount of about 15% to about 25% by weight of the loaded hydrogel film layer.
13. The oral care composition of claim 12 wherein the poly(N-vinyl lactam) is polyvinyl pyrrolidone present in an amount of about 35% to about 45% by weight of the loaded hydrogel film layer.
14. The oral care composition of claim 13 wherein the peroxide is hydrogen peroxide present in an amount of about 5% to about 10% by weight of the loaded hydrogel film layer.
15. The oral care composition of claim 11 wherein the substrate layer is constructed from wax to form a wax substrate layer, wherein the wax substrate layer and hydrogel film layer form a laminate.
16. The oral care composition of claim 15 wherein the hydrogel film layer is joined with a structural portion to form a laminate.