POLYOXYALKYLENE SILOXANE COPOLYMERS WITH ANTISTATIC PROPERTIES AND THEIR APPLICATION TO FIBERGLASS INSULATION AND OTHER SUBSTRATES
Polyoxyalkylene siloxane copolymer compositions and their application as antistatic agents to fiberglass insulation, textile, plastic, fiber optic, and electronics substrates are described. The polyoxyalkylene siloxane copolymer composition is made by the free radical polymerization of a vinyl polyoxyalkylene siloxane monomer with one or more organic unsaturated monomers. The vinyl polyoxyalkylene siloxane monomer has a linear, branched, or cyclic structure that may or may not be crosslinked. Aqueous solutions of the polyoxyalkylene siloxane copolymers provide improved wetting and uniform coverage on substrates. Treatment of fiberglass insulation with the polyoxyalkylene siloxane copolymers of the invention leads to improved antistatic properties and R-values.
1 . A method for reducing static in fiberglass insulation, textile, plastic, fiber optic, and electronics substrates comprising:
applying to the substrate an effective amount of a polyoxyalkylene siloxane copolymer, the polyoxyalkylene siloxane copolymer having linear, branched, or cyclic structures that may or may not be crosslinked,
the polyoxyalkylene siloxane copolymer having a viscosity less than about 60 centipoise and being prepared by free radical polymerization of a vinyl polyoxyalkylene siloxane containing one or more terminal vinyl groups with one or more organic unsaturated monomers, where the vinyl polyoxyalkylene siloxane monomer is
R 1 , R 2 , R 3 and/or R 4 being
or CH 3 with the exception that R 1 , R 2 , R 3 and R 4 groups are not CH 3 , and
x is an integer from 1-100
y is an integer from 0-100
a is an integer from 0-100
b is an integer from 0-100
c is an integer from 0-100; and
the one or more organic unsaturated monomers are
where R 5 is OH, NH 2 , or O— M+, where M+ is alkali metal salts, Na+, K+, Li+, alkaline-earth metal salts, ammonium salts or protonated amine salts of the monomer, and R 6 is H or CH 3 ,
2 . The method for reducing static of claim 1 in which the organic unsaturated monomer is:
where R 5 is OH, NH 2 , or O— M+ where M+ is alkali metal salts, Na+, K+, Li+, alkaline-earth metal salts, ammonium salts or protonated amine salts of the monomer, and R 6 is H or CH 3 .
3 . The method for reducing static of claim 1 in which the organic unsaturated monomer is:
4 . The method for reducing static of claim 1 in which the organic unsaturated monomer is:
5 . The method of claim 1 wherein the polyoxyalkylene siloxane copolymer is applied to the substrate as an aqueous solution at a solids level sufficient to deliver about 0.01 to 20 percent by weight of the polymer based on the weight of the substrate.
6 . The method of claim 1 wherein the polyoxyalkylene siloxane copolymer is applied to the substrate as an aqueous solution at a solids level sufficient to deliver about 0.01 to 5.0 percent by weight of the polymer based on the weight of the substrate.
7 . A method for reducing static in a fiberglass insulation substrate comprising:
applying to the substrate an effective amount of a polyoxyalkylene siloxane copolymer, the polyoxyalkylene siloxane copolymer having linear, branched, or cyclic structures that may or may not be crosslinked,
the polyoxyalkylene siloxane copolymer having a viscosity less than about 60 centipoise and being prepared by free radical polymerization of a vinyl polyoxyalkylene siloxane containing one or more terminal vinyl groups with one or more organic unsaturated monomers, where the vinyl polyoxyalkylene siloxane monomer is
R 1 , R 2 , R 3 and/or R 4 being
or CH 3 with the exception that R 1 , R 2 , R 3 and R 4 groups are not CH 3 , and
x is an integer from 1-100
y is an integer from 0-100
a is an integer from 0-100
b is an integer from 0-100
c is an integer from 0-100; and
the one or more organic unsaturated monomers are
where R 5 is OH, NH 2 , or O— M+, where M+ is alkali metal salts, Na+, K+, Li+, alkaline-earth metal salts, ammonium salts or protonated amine salts of the monomer, and R 6 is H or CH 3 ,
8 . The method for reducing static in fiberglass insulation of claim 7 in which the organic unsaturated monomer is:
where R 5 is OH, NH 2 , or O— M+ where M+ is alkali metal salts, Na+, K+, Li+, alkaline-earth metal salts, ammonium salts or protonated amine salts of the monomer, and R 6 is H or CH 3 .
9 . The method for reducing static in fiberglass insulation of claim 7 in which the organic unsaturated monomer is:
10 . The method for reducing static in fiberglass insulation of claim 7 in which the organic unsaturated monomer is:
11 . The method of claim 7 wherein the polyoxyalkylene siloxane copolymer is applied to the substrate as an aqueous solution at a solids level sufficient to deliver about 0.01 to 20 percent by weight of the polymer based on the weight of the substrate.
12 . The method of claim 7 wherein the polyoxyalkylene siloxane copolymer is applied to the substrate as an aqueous solution at a solids level sufficient to deliver about 0.01 to 5.0 percent by weight of the polymer based on the weight of the substrate.
13 . A static-reduced fiberglass substrate comprising:
fiberglass insulation surface-treated with an effective amount of a polyoxyalkylene siloxane copolymer having a viscosity less than about 60 centipoise prepared by free radical polymerization of a vinyl polyoxyalkylene siloxane containing one or more terminal vinyl groups with one or more organic unsaturated monomers, where the vinyl polyoxyalkylene siloxane monomer is
R 1 , R 2 , R 3 and/or R 4 being
or CH 3 with the exception that R 1 , R 2 , R 3 and R 4 groups are not CH 3 , and
x is an integer from 1-100
y is an integer from 0-100
a is an integer from 0-100
b is an integer from 0-100
c is an integer from 0-100; and
the one or more organic unsaturated monomers are
where R 5 is OH, NH 2 , or O— M+, where M+ is alkali metal salts, Na+, K+, Li+, alkaline-earth metal salts, ammonium salts or protonated amine salts of the monomer, and R 6 is H or CH 3 ,
14 . The static-reduced fiberglass substrate of claim 13 in which the organic unsaturated monomer is:
where R 5 is OH, NH 2 , or O— M+ where M+ is alkali metal salts, Na+, K+, Li+, alkaline-earth metal salts, ammonium salts or protonated amine salts of the monomer, and R 6 is H or CH 3 .
15 . The static reduced fiberglass substrate of claim 13 in which the organic unsaturated monomer is:
16 . The static reduced fiberglass substrate of claim 13 in which the organic unsaturated monomer is:
17 . The static-reduced fiberglass substrate of claim 13 wherein the fiberglass substrate is surface treated with about 0.01 to 20 percent by weight of the polyoxyalkylene siloxane copolymer based on the weight of the substrate.
18 . The static-reduced fiberglass substrate wherein the fiberglass substrate is surface treated with about 0.01 to 5.0 percent by weight of the polyoxyalkylene siloxane copolymers based on the weight of the substrate.
19 . A polyoxyalkylene siloxane copolymer having linear or cyclic structures that may or may not be crosslinked,
the polyoxyalkylene siloxane copolymer having a viscosity less than about 60 centipoise and being prepared by free radical polymerization of a vinyl polyoxyalkylene siloxane containing one or more terminal vinyl groups with one or more organic unsaturated monomers, where the vinyl polyoxyalkylene siloxane monomer is
R 1 , R 2 , R 3 and/or R 4 being
or CH 3 with the exception that R 1 , R 2 , R 3 and R 4 groups are not CH 3 , and
x is an integer from 1-100
y is an integer from 0-100
a is an integer from 0-100
b is an integer from 0-100
c is an integer from 0-100; and
the one or more organic unsaturated monomers are
where R 5 is OH, NH 2 , or O— M+, where M+ is alkali metal salts, Na+, K+, Li+, alkaline-earth metal salts, ammonium salts or protonated amine salts of the monomer, and R 6 is H or CH 3 ,
20 . A method for reducing static in fiberglass insulation, textile, plastic, fiber optic, and electronics substrates comprising:
applying to the substrate an effective amount of a polyoxyalkylene siloxane copolymer, the polyoxyalkylene siloxane copolymer having linear, branched, or cyclic structures that may or may not be crosslinked,
the polyoxyalkylene siloxane copolymer having a viscosity less than about 250 centipoise and being prepared by free radical polymerization of a vinyl polyoxyalkylene siloxane containing one or more terminal vinyl groups with one or more organic unsaturated monomers, where the vinyl polyoxyalkylene siloxane monomer is
R 1 , R 2 , R 3 and/or R 4 being
or CH 3 with the exception that R 1 , R 2 , R 3 and R 4 groups are not CH 3 , and
x is an integer from 1-100
y is an integer from 0-100
a is an integer from 0-100
b is an integer from 0-100
c is an integer from 0-100; and
the one or more organic unsaturated monomers are
where R 5 is OH or O— M+, where M+ is alkali metal salts, Na+, K+, Li+, alkaline-earth metal salts, ammonium salts or protonated amine salts of the monomer, and R 6 is H or CH 3 ,