Synthesis of conductive metal markings for chipless RFID applications
View Patent ↗A process for printing conductive metal markings directly on a substrate under an ambient condition, including the steps of synthesizing or providing conductive the ink on a substrate to form conductive metallic nanoparticles into an ink; and printing the ink on a substrate to form conductive metallic markings on the substrate. The printed conductive metallic markings may form wires that behave as resonant RFID antenna applications.
1. A method of printing conductive metal markings directly on a substrate comprising:
formulating an ink containing metallic nanoparticles, the ink having a viscosity of about 1 to about 100 centipoise;
printing the ink directly on the substrate under ambient conditions; and
annealing the ink to create the metal markings on the substrate,
wherein the metallic nanoparticles comprise copper nanoparticles stabilized with 2-butoxyethyl xanthate.
2. The method according to claim 1 , wherein formulating the ink containing the metallic nanoparticles comprises dispersing about 0.5 to about 35 weight % of the metallic nanoparticles in an ink vehicle.
3. The method according to claim 1 , wherein formulating the ink containing the metallic nanoparticles comprises dispersing about 20 weight % of the metallic nanoparticles in an ink vehicle.
4. The method according to claim 1 , further comprising forming printed metal markings on the substrate by depositing on the substrate the ink containing the metallic nanoparticles using an inkjet printer or a solid ink printer.
5. The method according to claim 4 , wherein the printed metallic markings are printed at a desired shape, size, and angle.
6. The method according to claim 5 , wherein the printed metallic markings are coded for a binary number.
7. The method according to claim 1 , wherein the printed metal markings form wires.
8. The method according to claim 7 , wherein the wires form resonant RFID antennas.
9. The method according to claim 1 , wherein the ink containing the metallic nanoparticles is annealed to the substrate at less than about 200° C.
10. The method according to claim 1 , wherein the ink containing the metallic nanoparticles is annealed to the substrate at about 120° C. to about 170° C.