COLLOIDAL TEMPLATING PROCESS FOR MANUFACTURE OF HIGHLY POROUS CERAMICS
A method for forming porous ceramic objects is provided, in which a suspension of ceramic precursor particles in a solution of gelatin is allowed to gel in the desired shape, and is then dried and sintered to the desired level of porosity.
1 . A method for making a porous ceramic object, comprising:
(a) preparing a suspension of ceramic precursor particles in an aqueous network-forming solution;
(b) shaping said suspension into a preform of the porous ceramic object;
(c) allowing said network-forming solution to gel, so as to form a solidified preform;
(d) drying said solidified preform; and
(e) sintering said preform at a temperature and for a time sufficient to cause said precursor particles to form a porous ceramic object;
wherein the network-forming solution comprises gelatin, and wherein the preform is sintered for a time sufficient for the ceramic object to attain a density between 40% and 90% of the maximum theoretical density.
2 . The method of claim 1 , wherein the amount of gelatin is between 5% and 40% by weight relative to water.
3 . The method of claim 2 , wherein the amount of gelatin is between 10% and 30% by weight relative to water.
4 . The method of claim 1 , wherein the preform is sintered until the ceramic object has a density between 50% and 80% of the maximum theoretical density.
5 . The method of claim 2 , wherein the preform is sintered until the ceramic object has a density between 50% and 80% of the maximum theoretical density.
6 . The method of claim 3 , wherein the preform is sintered until the ceramic object has a density between 50% and 80% of the maximum theoretical density.
7 . The method of any one of claims 1 - 6 , wherein the network-forming solution further comprises a pore-modifying agent.
8 . The method of claim 7 , wherein the pore-modifying agent is chitosan.
9 . The method of any one of claims 1 - 6 , wherein the shaping is accomplished by introducing the suspension into a mold.
10 . The method of any one of claims 1 - 6 , wherein a plurality of the ceramic particles comprise a ceramic precursor selected from the group consisting of metal oxides, mixed metal oxides, and silicon nitride.
11 . The method of claim 10 , wherein a plurality of the ceramic particles comprise a ceramic precursor selected from the group consisting of metal and mixed metal manganates and manganites, metal and mixed metal nickelates, metal and mixed metal cobaltites, metal and mixed metal chromates, lanthanum strontium manganate, lanthanum calcium manganate, yttrium stabilized zirconia, gadolinium-doped ceria, alumina, mullite, lanthanum strontium manganite, lanthanum strontium manganese cobaltite, lanthanum strontium ferrite cobaltite, samarium strontium cobaltite, and silicon nitride.
12 . The method of any one of claims 1 - 6 , wherein the ceramic object is a fuel cell electrode.
13 . A porous ceramic object prepared according to the method of any one of claims 1 - 6 .
14 . A fuel cell electrode prepared according to the method of any one of claims 1 - 6 .
15 . A porous ceramic object having a plurality of interconnected pores, wherein the pores have an average diameter between 5 μm and 20 μm and constitute between 10 and 60% of the volume of the object.
16 . The ceramic object of claim 15 , wherein the pores constitute between 20 and 50% of the volume of the object.
17 . The ceramic object of claim 16 , wherein the pores constitute between 30 and 40% of the volume of the object.