Separator and non-aqueous electrolyte secondary battery
View Patent ↗In a non-aqueous electrolyte secondary battery, a separator in which its dynamic hardness DH obtained when the load to an indenter reaches 12 kgf/cm 2 is 1000 or more is used. This separator includes at least one porous layer X including a polyolefin, and at least one porous layer Y including a heat resistant resin. The porosity of the porous layer X is 35% or more and 65% or less. In a pore size distribution of the porous layer X measured with a mercury porosimeter, a ratio of pores having a pore size of 0.02 μm or more and 0.2 μm or less is 40 vol % or more relative to a total pore volume. The thermal deformation temperature of the heat resistant resin is 160° C. or more.
1. A separator for a non-aqueous electrolyte secondary battery, comprising:
at least one porous layer X including a polyolefin, a porosity of said porous layer X being 35% or more and 65% or less, said porous layer X having a dynamic hardness DH of 1000 or more when the load to an indenter reaches 12 kgf/cm 2 ,
said polyolefin including a high density polyethylene and a low density polyethylene,
the amount of the high density polyethylene being 40 wt % or more relative to a total of the low density polyethylene and the high density polyethylene,
the specific gravity of the low density polyethylene being 0.93 or less and the specific gravity of the high density polyethylene being 0.94 or more,
wherein, in a pore size distribution of said porous layer X measured with a mercury porosimeter, a ratio of pores having a pore size of 0.02 μm or more and 0.2 μm or less is 30-75 vol % relative to a total pore volume.
2. The separator in accordance with claim 1 , comprising:
at least one porous layer Y including a heat resistant resin, a thermal deformation temperature of said heat resistant resin being 160° C. or more,
said thermal deformation temperature being a deflection temperature under load determined with a load of 1.82 MPa according to test method ASTM-D648 of American Society for Testing Materials.
3. A non-aqueous electrolyte secondary battery comprising a positive electrode, a negative electrode, a non-aqueous electrolyte, and the separator in accordance with claim 1 interposed between said positive electrode and said negative electrode.
4. The non-aqueous electrolyte secondary battery in accordance with claim 3 , wherein said positive electrode includes a positive electrode active material including a lithium-containing composite oxide; and
said composite oxide includes lithium, cobalt, nickel and aluminum.
5. The non-aqueous electrolyte secondary battery in accordance with claim 3 , wherein said negative electrode includes a negative electrode active material including silicon.
6. The separator in accordance with claim 1 , wherein said porous layer X has a dynamic hardness DH of 2000 or more and 8000 or less when the load to an indenter reaches 12 kgf/cm 2 .
7. The separator in accordance with claim 1 , wherein said porous layer X has a dynamic hardness DH of 3000 or more and 8000 or less when the load to an indenter reaches 12 kgf/cm 2 .