Flame retardant compositions containing mixtures of disubstituted phosphinate salts and monosubstituted phoshinate salts
A flame retarded thermoplastic polymer composition comprising a thermoplastic polymer and a mixture of metal salts of dialkylphosphinic and monoalkylphosphinic acid providing improved flame retardant performance and better processability compared to a similar composition containing only a salt of dialkylphosphinic acid.
1. A flame retardant thermoplastic polymer composition comprising a thermoplastic polymer and an effective flame retardant amount of a mixture of metal salts comprising (a) at least one metal salt of a disubstituted phosphinic acid of the general formula:
wherein R 1 and R 2 are the same or different linear or branched C 1 to C 15 alkyl,
and (b) at least one metal salt of a monosubstituted phosphinic acid of general formula
wherein R 3 is linear or branched C 1 to C 15 alkyl, and n is a valence of the metal M, and
wherein the concentration of the metal salt of monoalkylphosphinic acid is in the range of from about 0.5 to about 50 weight percent of the total weight of the mixture.
2. The composition of claim 1 wherein the thermoplastic polymer is a polyester.
3. The composition of claim 1 wherein the thermoplastic polymer is nylon.
4. The composition of claim 2 wherein the polyester is glass-filled polyester.
5. The composition of claim 2 wherein the polyester is selected from the group consisting of poly(butylene terephthalate) and poly(ethylene terephthalate).
6. The composition of claim 3 wherein the nylon is glass-filled nylon.
7. The composition of claim 1 wherein the thermoplastic polymer is a blend of polymers.
8. The composition of claim 7 wherein the blend of polymers is selected from the group consisting of a polyester/polycarbonate blend and a nylon/polyphenylene ether blend.
9. The composition of claim 1 wherein M is a multivalent metal selected from Groups II, III or IV of the Periodic Table or a transition metal.
10. The composition of claim 1 wherein M is aluminum.
11. The composition of claim 1 wherein the concentration of said at least one metal salt of a monosubstituted phosphinic acid is in the range of from about 3 to about 30 weight percent of the total weight of the mixture.
12. The composition of claim 1 wherein at least the at least one metal salt of the disubstituted phosphinic acid begins to volatilize at about 300° C. and substantially ceases volatilization at about 500° C.
13. The composition of claim 1 wherein the metal salts begin to volatilize at about 300° C. and substantially cease volatilization at about 400° C.
14. A flame retardant thermoplastic polymer composition comprising a thermoplastic polymer and an effective flame retardant amount of a mixture of metal salts comprising (a) at least one metal salt of a disubstituted phosphinic acid of the general formula:
and (b) at least one metal salt of a monosubstituted phosphinic acid of general formula
wherein R 1 , R 2 and R 3 are isobutyl, and n is a valence of the metal M.
15. A flame retardant thermoplastic polymer composition comprising a thermoplastic polymer and an effective flame retardant amount of a mixture of metal salts comprising a metal salt of a dialkylphosphinic acid and a metal salt of a monoalkylphosphinic acid, wherein said mixture of metal salts is present in an amount of from about 3 to about 30 weight percent based on the total weight of the thermoplastic polymer composition.
16. The composition of claim 15 wherein the mixture is present in an amount of from about 5 to about 20 weight percent of the total weight of the thermoplastic polymer composition.
17. A flame retardant thermoplastic polymer composition comprising a thermoplastic polymer and an effective flame retardant amount of a mixture of metal salts comprising an aluminum salt of monoisobutylphosphinic acid and an aluminum salt of diisobutylphosphinic acid.
18. A flame retardant composition comprising a mixture of an aluminum salt of monoisobutylphosphinic acid and an aluminum salt of diisobutylphosphinic acid.