Aromatic ether polymer, method for producing the same, and polymer composition
View Patent ↗Disclosed is a polymer which is useful for the preparation of an epoxy resin composition or a cured product thereof in film or sheet exhibiting high heat resistance, high thermal conductivity, low thermal expansion, high gas barrier property, and high toughness. The polymer is a thermoplastic aromatic ether polymer comprising a unit represented by the following general formula (1) at a ratio of 10 to 100 mol % and having a weight average molecular weight of 3,000 or more; in formula (1), X is an oxygen atom or a sulfur atom, R 1 and R 2 each is a hydrogen atom, an alkyl group of 1 to 8 carbon atoms, an aryl group, an alkoxy group, an aralkyl group, or a halogen atom, and n is a number of 1 to 3.
1. A crystalline structure comprising a thermoplastic aromatic ether polymer comprising a unit represented by the following general formula (1) at a concentration of 10 to 100 mol % and having a weight average molecular weight of 10,000 to 60,000;
in formula (1), X is oxygen atom or sulfur atom, R 1 and R 2 are hydrogen atoms, and n is 1,
wherein the benzene rings along the polymer backbone have a 1,4-phenylene structure,
wherein at least one of the terminal groups of the aromatic ether polymer is a hydroxyl group, and
wherein the polymer is in the crystallized state.
2. A method for producing the crystalline structure described in claim 1 which comprises reacting a diglycidyl compound represented by the following general formula (2)
with a bisphenol compound represented by general formula (3):
in general formula (2), X, R 1 , R 2 , and n are as defined in general formula (1); in general formula (3), m is a number of 1 to 3, R 3 and R 4 each is hydrogen atom, alkyl group of 1 to 8 carbon atoms, aryl group, alkoxy group, aralkyl group, or halogen atom, Y is direct bond, oxygen atom, sulfur atom, —SO—, —SO 2 —, —CO—, —CH 2 —, —CH(CH 3 )—, —C(CH 3 ) 2 —, —CH 2 -φ-CH 2 —, —CH(CH 3 )-φ-CH(CH 3 )—, —C(CH 3 ) 2 -φ-C(CH 3 ) 2 —, —CH 2 -φ-φ-CH 2 —, —CH(CH 3 )-φ-φ-CH(CH 3 )—, —C(CH 3 ) 2 -φ-φ-C(CH 3 ) 2 —, or 9,9-fluorenyl group, and φ is phenylene group.
3. A method for producing the crystalline structure described in claim 1 which comprises reacting a diglycidyl compound represented by the following general formula (4)
with a bisphenol compound represented by the following general formula (5):
in general formula (4), m is a number of 1 to 3, R 3 and R 4 each is hydrogen atom, alkyl group of 1 to 8 carbon atoms, aryl group, an alkoxy group, aralkyl group, or halogen atom, Y is direct bond, oxygen atom, sulfur atom, —SO—, —SO 2 —, —CO—, —CH 2 —, —CH(CH 3 )—, —C(CH 3 ) 2 —, —CH 2 -φ-CH 2 —, —CH(CH 3 )-φ-CH(CH 3 )—, —C(CH 3 ) 2 -φ-C(CH 3 ) 2 —, —CH 2 -φ-φ-CH 2 —, —CH(CH 3 )-φ-φ-CH(CH 3 )—, —C(CH 3 ) 2 -φ-φ-C(CH 3 ) 2 —, or 9,9-fluorenyl group, and φ is phenylene group; in general formula (5), X is oxygen atom or sulfur atom, R 1 and R 2 are hydrogen atoms, and n is 1.
4. A method for producing the crystalline structure described in claim 1 which comprises reacting a bisphenol compound represented by the following general formula (5)
with epichlorohydrin in the presence of an alkali metal hydroxide;
in general formula (5), X is oxygen atom or sulfur atom, R 1 and R 2 are hydrogen atoms, and n is 1.
5. The crystalline structure as described in claim 1 , wherein the polymer has a melting point in the range of 100° C. to 250° C.
6. The crystalline structure as described in claim 1 , wherein the polymer shows a heat of fusion of 10 J/g or more.
7. A resin composition comprising the crystalline structure described in any one of claims 1 , 5 , and 6 .
8. A cured resin composition obtained by curing the resin composition described in claim 7 .
9. A crystalline structure comprising a thermoplastic aromatic ether polymer comprising a unit represented by the following general formula (1) at a concentration of 10 to 100 mol % and having a weight average molecular weight of 3,000 or more;
in formula (1), X is oxygen atom or sulfur atom, R 1 and R 2 are hydrogen atoms, and n is 1,
wherein the benzene rings along the polymer backbone have a 1,4-phenylene structure,
wherein at least one of the terminal groups of the aromatic ether polymer is a hydroxyl group,
wherein the polymer is in the crystallized state; and
wherein the crystalline structure is produced by:
reacting a diglycidyl compound represented by the following general formula (2):
with a bisphenol compound represented by general formula (3):
in general formula (2), X, R 1 , R 2 , and n are as defined in general formula (1);
in general formula (3), m is a number of 1 to 3, R 3 and R 4 each is hydrogen atom, alkyl group of 1 to 8 carbon atoms, aryl group, alkoxy group, aralkyl group, or halogen atom, Y is direct bond, oxygen atom, sulfur atom, —SO—, —SO 2 —, —CO—, —CH 2 —, —CH(CH 3 )—, —C(CH 3 ) 2 —, —CH 2 -φ-CH 2 —, —CH(CH 3 )-φ-CH(CH 3 )—, —C(CH 3 ) 2 -φ-C(CH 3 ) 2 —, —CH 2 -φ-φ-CH 2 —, —CH(CH 3 )-φ-φ-CH(CH 3 )—, —C(CH 3 ) 2 -φ-φ-C(CH 3 ) 2 —, or 9,9-fluorenyl group, and φ is phenylene group;
wherein a molar ratio of the diglycidyl compound to the bisphenol compound is 1.1:1 to 1:1.1.