Production method of microporous polyethylene membrane and battery separator
View Patent ↗A microporous polyethylene membrane having well-balanced permeability, mechanical properties, heat shrinkage resistance, compression resistance, electrolytic solution absorbability, shutdown properties and meltdown properties, with an average pore diameter changing in a thickness direction is produced by melt-blending a polyethylene resin and a membrane-forming solvent to prepare a solution A having a resin concentration of 25 to 50% by mass and a solution B having a resin concentration of 10 to 30% by mass, the resin concentration in the solution A being higher than that in the solution B, (a) simultaneously extruding the resin solutions A and B through a die, cooling the resultant extrudate to provide a gel-like sheet in which the resin solutions A and B are laminated, and removing the membrane-forming solvent from the gel-like sheet, or (b) extruding the resin solutions A and B through separate dies, removing the membrane-forming solvent from the resultant gel-like sheets A and B to form microporous polyethylene membranes A and B, and alternately laminating the microporous polyethylene membranes A and B, while easily controlling the average pore diameter distribution in the microporous polyethylene membrane in a thickness direction.
1. A method for producing a microporous polyethylene membrane having an average pore diameter changing in a thickness direction, comprising the steps of melt-blending at least a polyethylene resin comprising ultra-high-molecular-weight polyethylene and high-density polyethylene, and a membrane-forming solvent to prepare a polyethylene resin solution A having a resin concentration of 25 to 50% by mass, melt-blending at least a polyethylene resin comprising the same ultra-high-molecular-weight polyethylene and high-density polyethylene as those in said polyethylene resin solution A, and a membrane-forming solvent to prepare a polyethylene resin solution B having a resin concentration of 10 to 30% by mass, the resin concentration in said polyethylene resin solution A being higher than that in said polyethylene resin solution B; simultaneously extruding said polyethylene resin solutions A and B through a die; cooling the resultant laminate extrudate to provide a gel-like sheet; and removing said membrane-forming solvent from said gel-like sheet.
2. A method for producing a microporous polyethylene membrane having an average pore diameter changing in a thickness direction, comprising the steps of melt-blending at least a polyethylene resin comprising ultra-high-molecular-weight polyethylene and high-density polyethylene, and a membrane-forming solvent to prepare a polyethylene resin solution A having a resin concentration of 25 to 50% by mass, melt-blending at least a polyethylene resin comprising the same ultra-high-molecular-weight polyethylene and high-density polyethylene as those in said polyethylene resin solution A, and a membrane-forming solvent to prepare a polyethylene resin solution B having a resin concentration of 10 to 30% by mass, the resin concentration in said polyethylene resin solution A being higher than that in said polyethylene resin solution B; extruding said polyethylene resin solutions A and B through separate dies; cooling the resultant extrudates to provide gel-like sheets A and B; removing said membrane-forming solvent from said gel-like sheets A and B to form microporous polyethylene membranes A and B; and alternately laminating said microporous polyethylene membranes A and B.
3. The method for producing a microporous polyethylene membrane according to claim 1 , wherein the resin concentration difference between said polyethylene resin solutions A and B is 5% or more by mass.
4. The method for producing a microporous polyethylene membrane according to claim 1 , wherein said ultra-high-molecular-weight polyethylene has a mass-average molecular weight of 7×10 5 or more, and said high-density polyethylene has a mass-average molecular weight of 1×10 4 or more and less than 5×10 5 .
5. The method for producing a microporous polyethylene membrane according to claim 1 , wherein each of the polyethylene resins for said polyethylene resin solution A and B is a composition comprising said ultra-high-molecular-weight polyethylene, said high-density polyethylene, and a heat-resistant resin having a melting point or glass transition temperature of 150° C. or higher.
6. The method for producing a microporous polyethylene membrane according to claim 5 , wherein said heat-resistant resin is polypropylene or polybutylene terephthalate.
7. The method for producing a microporous polyethylene membrane according to claim 2 , wherein the resin concentration difference between said polyethylene resin solutions A and B is 5% or more by mass.
8. The method for producing a microporous polyethylene membrane according to claim 2 , wherein said ultra-high-molecular-weight polyethylene has a mass-average molecular weight of 7×10 5 or more, and said high-density polyethylene has a mass-average molecular weight of 1×10 4 or more and less than 5×10 5 .