High-frequency coaxial cable
View Patent ↗In a high-frequency coaxial cable ( 1 ), an internal solid layer ( 3 ), an insulation layer ( 4 ) made of a foam resin, an external solid layer ( 5 ), and an external conductor ( 6 ) are provided on the periphery of an internal conductor ( 2 ) in this order. The external solid layer ( 5 ) has a dielectric dissipation factor of 1.0×10 −4 or less at 2 GHz. Thereby, the voltage standing-wave ratio and the attenuation of the high-frequency coaxial cable ( 1 ) are reduced.
1. A high-frequency coaxial cable comprising:
an inner solid layer, a foamed resin insulation layer, an outer solid layer and an outer conductor sequentially formed on an outer periphery of an inner conductor,
wherein the outer solid layer comprises a high-density polyethylene with a density of 0.960 g/cm 3 or more and a melt flow rate of 5 to 10 g/min, and a melting fracture tension of 10 to 50 mN, which is measured by using a capillary rheometer with a furnace body diameter of 9.55 mm under a condition of using a flat capillary with an inner diameter of 2.095 mm and a length of 8.03 mm with a piston speed of 10 mm/min at a temperature of 190° C. and a draw acceleration of 400 m/min 2 , and
wherein the outer solid layer has a thickness of 0.1 mm to 0.2 mm, and a dielectric tangent of 1.0×10 −4 or less at 2 GHz.
2. The high-frequency coaxial cable according to claim 1 , wherein the foamed resin insulation layer comprises 0.001 to 0.2 parts by weight of 4,4′-oxybisbenzenesulfonylhydrazide (OBSH) or azodicarbon amide (ADCA), or 0.001 to 0.2 parts by weight in total of both materials as a bubble nucleation agent, per 100 parts by weight of a resin as a main material.
3. The high-frequency coaxial cable according to claim 1 , wherein the foamed resin insulation layer contains an inert gas such as nitrogen or carbon dioxide gas solely or a mixed gas thereof as a foaming agent.
4. The high-frequency coaxial cable according to claim 1 , wherein a foaming degree of the foamed resin insulation layer is 70% or more.
5. The high-frequency coaxial cable according to claim 1 , wherein the inner solid layer comprises a composite of a low density polyethylene and an ultralow density polyethylene having a density lower than that of the low density polyethylene which is graft-copolymerized with a maleic anhydride.
6. The high-frequency coaxial cable according to claim 2 , wherein the foamed resin insulation layer contains an inert gas such as nitrogen or carbon dioxide gas solely or a mixed gas thereof as a foaming agent.