MAGNETIC RECORDING DISK AND METHOD FOR MANUFACTURE THEREOF
In a magnetic recording disk 1 including a magnetic layer 12 , a protective layer 13 , and a lubricating layer 14 , the lubricating layer 14 is made from a lubricant prepared from a composition. The weight change of the lubricant ranges from −20% to −50% at 300° C. in the case where the lubricant is subjected to thermogravimetric analysis in such a manner that the lubricant is heated from 40° C. to 500° C. at a heating rate of 10° C./min. The lubricant has a maximum peak at about 300° C. in the case where the lubricant is subjected to differential thermal analysis in the same manner as described above. The lubricant can be quantitatively measured for heat resistance. Therefore, a magnetic recording disk exhibiting stable performance at high temperatures and a method for manufacturing such a magnetic recording disk can be obtained.
1 . A magnetic recording disk comprising a nonmagnetic substrate, a magnetic layer, a protective layer, and a lubricating layer, these layers being arranged on the nonmagnetic substrate in that order,
wherein the lubricating layer is made from a lubricant, the weight change of the lubricant ranges from −20% to −50% at 300° C. in the case where the lubricant is subjected to thermogravimetric analysis in such a manner that the lubricant is heated from 40° C. to 500° C. at a heating rate of 10° C./min, and the lubricant has a maximum peak at about 300° C. in the case where the lubricant is subjected to differential thermal analysis in the same manner as described above.
2 . The magnetic recording disk according to claim 1 , wherein the weight change of the lubricant ranges from −25% to −40%.
3 . The magnetic recording disk according to claim 1 , wherein the lubricant is prepared from a composition containing a perfluoropolyether compound which is a principal component and which is represented by the following formula:
[In the above formula, p and q are natural numbers.]
4 . A method for manufacturing a magnetic recording disk including a nonmagnetic substrate, a magnetic layer, a protective layer, and a lubricating layer, these layers being arranged on the nonmagnetic substrate in that order, the method comprising a step of preparing a lubricant by purifying a composition containing a perfluoropolyether compound which is a principal component and a step of forming the lubricating layer from the lubricant,
wherein the weight change of the lubricant ranges from −20% to −50% at 300° C. in the case where the lubricant is subjected to thermogravimetric analysis in such a manner that the lubricant is heated from 40° C. to 500° C. at a heating rate of 10° C./min, the lubricant has a maximum peak at about 300° C. in the case where the lubricant is subjected to differential thermal analysis in the same manner as described above, and the perfluoropolyether compound is represented by the following formula:
[In the above formula, p and q are natural numbers.]
5 . The magnetic recording disk according to claim 2 , wherein the lubricant is prepared from a composition containing a perfluoropolyether compound which is a principal component and which is represented by the following formula:
[In the above formula, p and q are natural numbers.]