Silane-Sulfide Chain End Modified Elastomeric Polymers
A chain end modified polymer comprising the reaction product of a living anionic elastomeric polymer and a silane-sulfide modifier A preferred class of modifiers includes compounds represented by the formula: (RO) x (R) y Si—R′—S—SiR 3 , wherein Si is silicon; S is sulfur; O is oxygen; x is an integer selected from 1, 2 and 3; y is an integer selected from 0, 1, and 2; x+y=3; R is the same or different and is: (C 1 -C 16 ) alkyl; and R′ is aryl, alkylaryl, or (C 1 -C 16 ) alkyl. The invention further includes methods for making such chain end modified polymers, their use in preparing vulcanized elastomeric polymer compositions, and articles made from such compositions, including pneumatic tires, tire treads, belts, and the like. The subject compositions exhibit lower Tan δ at 60° C. values, while maintaining good processing characteristics, and a good balance of physical properties, including: abrasion resistance, tensile strength, modulus and elongation at break.
1 . A chain end modified elastomeric polymer, comprising the reaction product of:
i) a living anionic elastomeric polymer, and
ii) a silane-sulfide modifier represented by the formula:
(RO) x (R) y Si—R′—S—SiR 3
wherein:
Si is silicon; S is sulfur; O is oxygen; x is an integer selected from 1, 2 and 3;
y is an integer selected from 0, 1, and 2; x+y=3;
R is the same or different and is (C 1 -C 16 ) alkyl; and R′ is aryl, and alkyl aryl, or (C 1 -C 16 ) alkyl.
2 . The chain end modified elastomeric polymer of claim 1 , wherein R′ is a (C 1 -C 16 ) alkyl.
3 . The chain end modified elastomeric polymer of claim 1 , wherein each R group is the same or different, and each is independently a (C 1 -C 5 ) alkyl, and wherein R′ is (C 1 -C 5 ) alkyl.
4 . The chain end modified elastomeric polymer of claim 1 , wherein the reaction product further comprises at least one coupling agent, selected from the group consisting of tin halide, tin alkoxide, silicon halide, and silicon alkoxide.
5 . The chain end modified elastomeric polymer of claim 1 , wherein the modified elastomeric polymer is selected from the group consisting of modified homopolymers of isoprene, modified homopolymers of butadiene, modified copolymers of butadiene with styrene, modified copolymers of isoprene with styrene, modified terpolymers butadiene with isoprene and styrene, and combinations thereof.
6 . A vulcanized elastomeric polymer composition comprising the reaction product of the following:
1) a filler;
2) a vulcanization agent; and
3) a chain end modified elastomeric polymer, and wherein the chain end modified elastomeric polymer is the reaction product of:
i) a living anionic elastomeric polymer, and
ii) a silane-sulfide modifier represented by the formula:
(RO) x (R) y Si—R′—S—SiR 3
wherein:
Si is silicon; S is sulfur; O is oxygen;
x is an integer selected from 1, 2 and 3;
y is an integer selected from 0, 1, and 2; x+y=3;
R is the same or different and is: (C 1 -C 16 ) alkyl; and
R′ is aryl, alkylaryl, or (C 1 -C 16 ) alkyl.
7 . The composition of claim 6 , wherein R′ is a (C 1 -C 16 ) alkyl.
8 . The composition of claim 6 , further comprising an oil.
9 . The composition of claim 6 , wherein each R group is the same or different, and each is a (C 1 -C 5 ) alkyl, and wherein R′ is (C 1 -C 5 ) alkyl.
10 . The composition of claim 6 , wherein the reaction product further comprises at least one coupling agent, selected from the group consisting of tin halide, tin alkoxide, silicon halide, and silicon alkoxide.
11 . The composition of claim 6 , wherein the filler comprises silica.
12 . The composition of claim 6 , wherein the filler comprises carbon black.
13 . The composition of claim 6 wherein the chain end modified elastomeric polymer is selected from the group consisting of modified homopolymers of isoprene, modified homopolymers of butadiene, modified copolymers of butadiene with styrene, modified copolymers of isoprene with styrene, modified terpolymers butadiene with isoprene and styrene, and combinations thereof.
14 . The composition of claim 6 , comprising from 10 to 100 parts by weight filler, and from 0.5 to 10 parts by weight of vulcanization agent, both based upon 100 parts by weight of total elastomeric polymer.
15 . A tire tread comprising the vulcanized elastomeric polymer composition of claim 6 .
16 . A method for making a vulcanized elastomeric polymer composition, said method comprising combining at least the following constituents:
1) a filler;
2) a vulcanization agent; and
3) a chain end modified elastomeric polymer which is the reaction product of:
i) a living anionic elastomeric polymer, and
ii) a silane-sulfide modifier represented by the formula:
(RO) x (R) y Si—R′—S—SiR 3
wherein:
Si is silicon; S is sulfur; O is oxygen;
x is an integer selected from 1, 2 and 3;
y is an integer selected from 0, 1, and 2; x+y=3;
R is the same or different and is: (C 1 -C 16 ) alkyl; and
R′ is aryl, alkylaryl, or (C 1 -C 16 ) alkyl.
17 . The method of claim 16 , wherein R′ is a (C 1 -C 16 ) alkyl.
18 . The method of claim 16 , wherein the composition further comprises an oil.
19 . A composition comprising the following: (a) the chain end modified elastomeric polymer of claim 1 , and (b) an oil.
20 . The chain end modified elastomeric polymer of claim 1 , wherein the modified elastomeric polymer is selected from the group consisting of modified homopolymers of butadiene and modified copolymers of butadiene with styrene.
21 . The composition of claim 6 wherein the chain end modified elastomeric polymer is selected from the group consisting of modified homopolymers of butadiene and modified copolymers of butadiene with styrene.
22 . The chain end modified elastomeric polymer of claim 1 , wherein the living anionic elastomeric polymer is selected from the group consisting of homopolymers of isoprene, homopolymers of butadiene, copolymers of butadiene with styrene, copolymers of isoprene with styrene, terpolymers butadiene with isoprene and styrene, and combinations thereof.
23 . The composition of claim 6 , wherein the living anionic elastomeric polymer is selected from the group consisting of homopolymers of isoprene, homopolymers of butadiene, copolymers of butadiene with styrene, copolymers of isoprene with styrene, terpolymers butadiene with isoprene and styrene, and combinations thereof.