Method for forming an electrocatalytic surface on an electrode and the electrode
View Patent ↗The invention relates to a method of forming an electrocatalytic surface on an electrode in a simple way, in particular on a lead anode used in the electrolytic recovery of metals. The catalytic coating is formed by a spraying method which does not essentially alter the characteristics of the coating powder during spraying. Transition metal oxides are used as the coating material. After the spray coating the electrode is ready for use without further treatment. The invention also relates to an electrode onto which an electrocatalytic surface is formed.
1. An electrocatalytically coated electrode, wherein a coating made up mainly of a manganese oxide has been formed on the surface of a lead based anode used in the electrolytic recovery of metals by cold-spraying, the manganese oxide being at least one of the following: beta-manganese dioxide (β-MnO 2 ), chemically manufactured manganese dioxide (CMD), electrochemically manufactured manganese dioxide (EMD), heat-treated (HTMD) or natural manganese dioxide (NMD).
2. An electrode according to claim 1 , wherein the oxide to be used as a coating is a simple oxide or a synthesized one, where a variant oxide of the same metal is attached to the first metal oxide.
3. An electrode according to claim 1 , wherein the oxide to be used as a coating is a synthesized one, where one or several oxides of another transition metal are attached to the first metal oxide.
4. An electrode according to claim 1 , wherein the manganese oxide has been combined with a transition metal being in the form of MO 2 , MO 3 , M 3 O 4 or M 2 O 5 , where M is a transition metal.
5. An electrode according to claim 4 , wherein the transition metal is at least one of the following: PtO 2 , RuO 2 , IrO 2 , Co 3 O 4 , NiCo 2 O 4 , CoFe 2 O 4 , NiO 2 , TiO 2 , perovskites, Ta 2 O 5 , WO 3 , or MoO 3 .
6. An electrode according to claim 1 , wherein the manganese oxide has been combined with PbO 2 or SnO 2 .
7. An electrode according to claim 1 , wherein the thickness of the coating to be formed on the electrode is 1-5 times the diameter of the coating powder particle.
8. A method for forming an electrocatalytic surface on an electrode, wherein a catalyst coating in powder form is cold-sprayed in one step on the surface of a lead based anode used in an electrolytic recovery of metals, the coating comprising mainly of a manganese dioxide, being at least one of the following: beta-manganese dioxide (β-MnO 2 ) , chemically manufactured manganese dioxide (CMD), electrochemically manufactured manganese dioxide (EMD), heat-treated (HTMD) or natural manganese dioxide (NMD).
9. A method according to claim 8 , wherein the physical and chemical properties of the catalyst in powder form remain essentially unchanged during spraying.
10. A method according to claim 8 , wherein the oxide to be used as a coating is a simple oxide or a synthesized one, where a variant oxide of the same metal is attached to the first metal oxide.
11. A method according to claim 8 , wherein the oxide to be used as a coating is a synthesized one, where one or several oxides of another transition metal are attached to the first metal oxide.
12. A method according to claim 8 , wherein the manganese oxide is combined with a transition metal being in the form of MO 2 , MO 3 , M 3 O 4 , M 2 O 5 , where M is a transition metal.
13. A method according to claim 12 , wherein the transition metal is at least one of the following: PtO 2 , RuO 2 , IrO 2 , Co 3 O 4 , NiCo 2 O 4 , CoFe 2 O 4 , NiO 2 , TiO 2 , perovskites, Ta 2 O 5 , WO 3 , or MoO 3 .
14. A method according to claim 8 , wherein the manganese oxide is combined with PbO 2 or SnO 2 .
15. A method according to claim 8 , wherein the particle size of the powder to be used in coating is in the region of 5-100 micrometers.
16. A method according to claim 8 , wherein the thickness of the coating to be formed on the electrode is 1-5times the diameter of the coating powder particle.
17. A method according to claim 8 , wherein the electrode is cleaned chemically and/or mechanically before the formation of the coating on the electrode.