Process of fabricating three-dimensional object
View Patent ↗A light beam is irradiated to sinter powder layers into a plurality of cured layer which are superimposed to each other to fabricate a three-dimensional object. A portion forming an outer shell of the object is given by high-density cured layers, while the other portion is given by low-density cured layers. The high-density cured layer making up at least a side of the object is composed of a high-density primary cured layer obtained by irradiation of a primary irradiation to the powder layer, and a high-density secondary layer obtained by a secondary irradiation to a supplemental powder layer supplied on the high-density primary cured layer. Thus, the high-density cured layer is given a height in level with the low-density cured layer, which assures constant height of each cured layer which is a combination of the high-density cured layer and the low-density cured layer.
1. A process of fabricating a three-dimensional object, said process comprising the following sequential steps of:
a) providing a powder layer made of a powder material to have a uniform thickness;
b) irradiating a light beam to a selected portion of said powder layer to sinter or melt said selected portion into a cured layer;
c) providing an additional powder layer on said cured layer;
d) irradiating said light beam to a selected portion of said additional powder layer to form an additional cured layer consolidated with said cured layer; and
e) repeating the steps of c) and d) in order to stack said cured layers to provide said three-dimensional object,
wherein said cured layer comprises a first cured portion and a second cured portion having a lower density than said first cured portion,
wherein a vertically movable elevation stage is utilized to hold said cured layer, said elevation stage being lowered before every step of c) so as to be supplied with said powder material, thereby forming thereon the powder layer of uniform thickness, and
wherein said process is further characterized by the following sequential steps of:
i) making a primary irradiation of irradiating said light beam to an outline area of at least one of said powder layers forming an outer shell of said three-dimensional object in order to form a primary cured layer as a part of said first cured portion;
ii) supplying an extra amount of said powder on top of said primarily cured layer of which thickness is reduced as a result of being cured with the elevation stage kept in the same level as in said step i), so as to provide a supplemental powder layer of a uniform thickness on said primary cured layer;
iii) making a secondary irradiation of irradiating said light beam to at least one portion of said supplemental powder layer in order to form a secondary cured layer as a part of said first cured portion, said secondary cured layer consolidated to said primarily cured layer; and
iv) irradiating said light beam to a remaining portion of said powder layer confined by said outline area and not converted into said primary cured layer in order to form a low-density cured layer as said second cured portion.
2. A process of fabricating a three-dimensional object as set forth in claim 1 , wherein
said secondary irradiation is made to irradiate said light beam only to a portion of said supplemental powder layer not overlapping with a subsequently cured layer superimposed thereon so as to form said high-density secondary cured layer, and said primary irradiation is made to consolidate the portion of said supplemental powder layer overlapping with the subsequently superimposed cured layer into said high-density primary cured layer in said subsequently superimposed cured layer together with a powder layer supplied on said supplemental powder layer for the formation of said subsequently superimposed cured layer.
3. A process of fabricating a three-dimensional object as set forth in claim 1 , wherein
said powder material is supplied onto said primary cured layer with said elevation stage kept in the fixed level in order to prepare said supplemental powder layer of which top surface is in level with that of not-yet-sintered or not-yet-melted powder layer confined by said outline area.
4. A process of fabricating a three-dimensional object as set forth in claim 1 , wherein
said primary irradiation and said secondary irradiations are made to scan said light beams respectively in directions crossing with each other.
5. A process of fabricating a three-dimensional object as set forth in claim 1 , wherein
each said primary irradiation and said secondary irradiations is made by said light beam with an irradiation energy which is constant per unit time as well as per unit volume of the powder being sintered or melted.
6. A process of fabricating a three-dimensional object as set forth in claim 1 , wherein
for the formation of the cured layer not overlapping with the subsequently superimposed cured layer, the light beam is irradiated to said high-density primary cured layer over an irradiation range which is different from an irradiation range over which the light beam is irradiated to form said high-density secondary cured layer, and
said individual irradiation ranges are determined by a settling thickness which is the thickness of the powder layer minus the thickness of said primary cured layer.
7. A process of fabricating a three-dimensional object as set forth in claim 2 , wherein
said primary irradiation and said secondary irradiations are made to scan said light beams respectively in directions crossing with each other.
8. A process of fabricating a three-dimensional object as set forth in claim 2 , wherein
each said primary irradiation and said secondary irradiations is made by said light beam with an irradiation energy which is constant per unit time as well as per unit volume of the powder being sintered or melted.
9. A process of fabricating a three-dimensional object as set forth in claim 2 , wherein
for the formation of the cured layer not overlapping with the subsequently superimposed cured layer, the light beam is irradiated to said high-density primary cured layer over an irradiation range which is different from an irradiation range over which the light beam is irradiated to form said high-density secondary cured layer, and
said individual irradiation ranges are determined by a settling thickness which is the thickness of the powder layer minus the thickness of said primary cured layer.
10. A process of fabricating a three-dimensional object as set forth in claim 1 , each of said primary cured layer and said secondary cured layer having a porosity of 5% or less, said low-density cured layer having a porosity of more than 5%.