Storage-stable coating composition for abrasion-resistantly and weathering-stably providing smooth inorganic surfaces with easy-to-clean properties
View Patent ↗The present invention relates to a special coating composition based on components a) at least one hydrolyzable fluoroalkylsilane of the formula (I) CF3(CF2)n(CH2)2Si(CH3)yX3-y (I), in which X is a group from the series chlorine, methoxy, ethoxy, isopropoxy, and n-propoxy and n is a number from the series 3, 4, 5, 6, 7, 8, and 9, and y is 0 or 1, b) HC1, c) water, d) isopropanol, and e) dodecane, and on a silane component (a): water molar ratio of 1:4.5 to 1:9. The invention further relates to a process for preparing such a composition and also to its use for providing smooth, inorganic substrate surfaces with an abrasion-resistant and weathering-stable easy-to-clean coating.
1. A coating composition based on components
a) at least one hydrolyzable fluoroalkylsilane of the general formula (I)
CF 3 (CF 2 ) n (CH 2 ) 2 Si(CH 3 ) y X 3-y (I),
in which X is a group from the series chlorine, methoxy, ethoxy, isopropoxy, and n-propoxy and n is a number from the series 3, 4, 5, 6, 7, 8, and 9, and y is 0 or 1,
b) HCl,
c) water,
d) isopropanol, and
e) dodecane,
and on a silane component (a): water molar ratio of 1:4.5 to 1:9.
2. The composition as claimed in claim 1 , comprising
a) 20 parts by weight of fluoroalkylsilane component of the formula (I),
b) 0.05 to 0.15 part by weight of HCl,
c) 3.2 to 6.4 parts by weight of H 2 O,
d) 500 to 1000 parts by weight of isopropanol, and
e) 30 to 60 parts by weight of dodecane.
3. The composition as claimed in claim 1 , wherein the silane component (a): water molar ratio is 1:5.3 to 1:5.8.
4. The coating composition as claimed in claim 1 , which is prepared by diluting the silane component (a) with isopropanol and subjecting it in the presence of HCl to partial hydrolysis and also to condensation, the silane component (a): water molar ratio being 1:4.5 to 1:9, and subsequently diluting the reaction mixture thus obtained with an isopropanol- and dodecane-containing mixture.
5. A process for preparing a coating composition as claimed in claim 1 ,
which comprises
diluting the silane component (a) with isopropanol, then adding water and then hydrochloric acid, stirring the mixture thus obtained for 1 to 4 hours at a temperature of 0 to 80° C., the hydrolysis step being based on a silane component (a): water molar ratio of 1:4.5 to 1:9, and subsequently diluting the reaction mixture with a mixture of isopropanol and dodecane
or
comprises adding silane component (a) to a mixture of isopropanol, water and hydrochloric acid, stirring the mixture thus obtained for 1 to 4 hours at a temperature of 0 to 80° C., the hydrolysis step being based on a silane component (a): water molar ratio of 1:4.5 to 1:9, and subsequently diluting the reaction mixture with a mixture of isopropanol, dodecane, and hydrochloric acid.
6. The process as claimed in claim 5 , wherein the components are employed in the following amounts:
a) 20 parts by weight of fluoroalkylsilane of formula (I),
b) 0.05 to 0.15 part by weight of HCl,
c) 3.2 to 6.4 parts by weight of H 2 O,
d) 500 to 1000 parts by weight of isopropanol, and
e) 30 to 60 parts by weight of dodecane.
7. The process as claimed in claim 5 ,
wherein 1 to 1.5 parts by weight of component (d) are used per part by weight of component (a) in the hydrolysis step.
8. The process as claimed in claim 5 ,
wherein 40% to 100% by weight of component (b) is used in the hydrolysis step.
9. The process as claimed in claim 5 ,
wherein n-dodecane or an isomer mixture of C 12 -hydrocarbons having a boiling range of from >180° C. is used as component (e).
10. The process as claimed in claim 5 ,
wherein the hydrolysate is diluted with a mixture of component (e) and the remainder of component (d) or with a mixture of component (e), the remainder of component (d), and the remainder of component (b).
11. A method for providing smooth, substantially inorganic substrate surfaces with an abrasion-resistant and weathering-stable easy-to-clean coating comprising using as a coating the composition as claimed in claim 1 .
12. The method as claimed in claim 11 , wherein the substrate of the surface to be treated is selected from glass, glazes, minerals, metal, ceramic, polycarbonate, polymethyl methacrylate, polyurethane, and polystyrene.