Synthesis of lizardite from olivine
View Patent ↗Methods of converting olivine to lizardite without formation of chrysotile or brucite are disclosed. The methods comprise heating a mixture of olivine, silica, water, and a caustic agent. The addition of silica allows for complete conversion of the olivine to lizardite through a more thermodynamically favorable reaction. The olivine and silica are preferably of small particle size to increase reactivity.
1. A process for synthesizing lizardite from olivine, comprising:
providing a reaction mixture comprising olivine, silica, water, and a caustic agent selected from the group consisting of sodium hydroxide and potassium hydroxide; and
heating the reaction mixture for a period of time to obtain lizardite, which is free of chrysotile.
2. The process of claim 1 , wherein the caustic agent is present in an amount of at least 21 weight percent of the liquid phase of the reaction mixture.
3. The process of claim 1 , wherein the caustic agent is present in an amount of from about 25 weight percent to about 33 weight percent of the liquid phase of the reaction mixture.
4. The process of claim 1 , wherein the reaction mixture is heated at a temperature of about 170° C. or higher.
5. The process of claim 1 , wherein the reaction mixture is heated at a temperature from about 170° C. to about 210° C.
6. The process of claim 1 , wherein the period of time is about 12 hours or longer.
7. The process of claim 1 , wherein the period of time is from about 12 hours to about 24 hours.
8. The process of claim 1 , wherein the molar ratio of olivine to silica is approximately 3:1.
9. The process of claim 1 , further comprising washing the olivine with an acid prior to providing the olivine to the reaction mixture.
10. The process of claim 1 , further comprising modifying the surface of the lizardite.
11. The process of claim 10 , wherein the surface is modified with an additive selected from the group consisting of silanes, titanates, and surfactants.
12. The process of claim 1 , further comprising separating the lizardite from the reaction mixture.
13. The process of claim 1 , wherein the resulting lizardite has an average diameter of less than 1 micron and a thickness of from about 30 to about 80 nanometers.
14. The process of claim 1 , wherein the resulting lizardite has a BET surface area of 10 m 2 /g or more.
15. The process of claim 1 , further comprising washing the lizardite with an acid.
16. The process of claim 1 , wherein the reaction mixture further comprises a salt.
17. The process of claim 16 , wherein the salt comprises a Al, Mg, or Li cation.
18. A process for synthesizing lizardite from olivine, comprising:
providing a reaction mixture comprising olivine, silica, water, and a caustic agent selected from the group consisting of sodium hydroxide and potassium hydroxide, wherein the molar ratio of olivine to silica is approximately 3:1; and
heating the reaction mixture at a temperature of about 170° C. or higher for a period of about 12 hours or longer to obtain lizardite which is substantially free of chrysotile.