Variable felted polyurethane foams for sponges and wipes
View Patent ↗A polyurethane foam sponge that picks up at least 80% of water in a wipe dry performance test is made by variably felting (compressing under heat and pressure) a foam sheet to a compression ratio of about 1.05 to 2.9. The resulting foam sponge has from 5% to 25% of its top and bottom surface portions modified by the variable felting, while its core portion remains substantially unmodified.
1. A method for making a hydrophilic polyurethane foam, comprising:
variably felting a sheet of polyurethane foam having a top surface and a bottom surface by compressing the foam in a direction parallel to its foam rise direction at a compression ratio of about 1.05 to 1.2 and at a temperature in the range of about 340 to about 450° F. (171 to 232° C.) for about 10 to about 22 minutes so as to cause from the top surface to a depth of from about 5% to about 25% of the thickness and from the bottom surface to a depth of from about 5% to about 25% of the thickness to have a felted structure,
wherein the felted polyurethane foam absorbs water.
2. The method of claim 1 , wherein the sheet of polyurethane foam is variably felted at a temperature in the range of about 340 to about 380° F. (171 to 193° C.).
3. The method of claim 1 , wherein the variably felting is carried out to cause solely from 5% to 25% of the top surface and solely from 5% to 25% of the bottom surface to have a felted structure.
4. The method of claim 1 , wherein the as felted polyurethane foam has wipe dry water pick up of at least about 80% of water in a wipe dry performance test exposing an 11.2 cm by 7.7 cm by 1.5 cm sponge of the felted polyurethane foam to 30 g of water for 4 seconds.
5. The method of claim 1 , further comprising reticulating the polyurethane foam prior to variably felting.
6. The method of claim 1 , wherein the polyurethane foam is formed with a polyol selected from the group consisting of one or more polyester polyols, one or more hydrophilic polyester polyols, and mixtures thereof.
7. The method of claim 1 , wherein the polyurethane foam is formed from a foam composition that incorporates one or more double cell additives.
8. The method of claim 1 , wherein the polyurethane foam is formed from a foam composition that incorporates one or more wetting agents.
9. The method of claim 1 , wherein before felting, the polyurethane foam has pore sizes in the range of 70 to 130 pores per linear inch (27.6 to 51 pores per cm).
10. A hydrophilic polyurethane foam made according to the method of claim 1 .
11. A sponge, mop, or industrial wipe, comprising the hydrophilic foam of claim 10 .
12. An absorbent article or absorbent component, comprising:
a single hydrophilic polyurethane foam sheet of one foam composition, said sheet having a top surface, a bottom surface and a thickness between the top surface and the bottom surface, wherein foam from the top surface to a depth of only from about 5% to about 25% of the thickness is felted, and wherein foam from the bottom surface to a depth of only from about 5% to about 25% of the thickness is felted, wherein remaining foam between the top surface and the bottom surface of from about 50% to about 90% of the thickness remains unfelted, and wherein said sheet is made by the method of claim 1 .