Method of making a deposit on an SiC-covered substrate
View Patent ↗The invention relates to a method of depositing a coating on a part having its surface made of silicon carbide. The method comprises the following steps: a) applying laser treatment to the SiC surface by superposing laser impacts for the purpose of increasing the roughness of said surface; and b) depositing a coating on the SiC surface by atmospheric thermal spraying. The invention also provides a device for measuring deformation, which device comprises a first alumina coating obtained by atmospheric thermal spraying onto the silicon carbide layer covering the substrate of the part after it has been treated by superposing laser impacts, a free filament strain gauge placed on the coating, and an additional alumina coating obtained by atmospheric thermal spraying onto the strain gauge.
1. A method of making a deformation measurement device, the method comprising the following steps:
a) applying laser treatment to the SiC surface of a part constituted by a substrate covered in an SiC layer deposited by chemical vapor deposition, the laser treatment comprising superposing laser impacts for the purpose of increasing the roughness of said surface;
b) depositing an alumina coating on said SiC surface by atmospheric thermal spraying;
c) placing a free filament strain gauge on said coating, the gauge being held on its support, and said support having openings;
d) depositing a second alumina coating on the strain gauge and on the coating by atmospheric thermal spraying through said openings;
e) removing said support; and
f) depositing a third coating of alumina by atmospheric thermal spraying on said first coating, on said second coating, and on said strain gauge.
2. The method according to claim 1 , wherein the laser is an Nd:YAG laser having a pulse duration of 10 ns, the number of laser impacts per surface point lying in the range 200 to 500, and the fluence of the laser being 2 J/cm 2 .
3. The method according to claim 1 , wherein the atmospheric thermal spraying is selected between plasma spraying and flame spraying.
4. The method according to claim 1 , wherein said substrate is selected between a composite material having a silicon carbide matrix and a composite material having a self-healing ceramic matrix.