View Patent ↗Sintered, spherical composite pellets or particles comprising alumina fines, at least one of clay and bauxite and optionally a sintering aid, are described, along with a process for their manufacture. The use of such pellets in hydraulic fracturing of subterranean formations and in grinding is also described.
1. A method for making a gas and oil well proppant comprising a plurality of sintered, spherical pellets comprising preparing a composition comprising from about 58 to about 75 percent by weight of alumina fines and from about 25 to about 42 percent by weight of clay, wherein the alumina fines has an alumina content of about 99 percent by weight.
2. The method of claim 1 wherein the composition further comprises at least one sintering aid.
3. The method of claim 2 , wherein the at least one sintering aid is selected from the group consisting of iron oxide, zinc oxide, bentonite clay, feldspar, nepheline syenite, talc, titanium oxide, lithium carbonate, sodium oxide, sodium carbonate, sodium silicates, magnesium oxide, magnesium carbonate, calcium oxide, calcium carbonate, manganese oxide, boric acid, boron carbide, aluminum diboride, boron nitride and boron phosphide.
4. The method of claim 2 , wherein the composition comprises from about 0.1 to about 15 percent by weight of the at least one sintering aid.
5. The method of claim 2 , wherein the composition comprises from about 1 to about 8 percent by weight of the at least one sintering aid.
6. The method of claim 1 , wherein the composition comprises kaolin clay.
7. The method of claim 1 , wherein the composition comprises calcined kaolin clay.
8. The method of claim 1 , wherein the composition comprises 58 percent by weight of alumina fines and 42 percent by weight of clay.
9. The method of claim 2 , wherein the composition comprises 64 percent by weight of alumina fines, 28 percent by weight of clay and 8 percent by weight of the at least one sintering aid.
10. The method of claim 9 , wherein the at least one sintering aid comprises iron oxide.
11. The method of claim 1 , wherein the pellets have an apparent specific gravity of from about 2.70 to about 3.75.
12. The method of claim 1 , wherein the pellets have a bulk density of from about 1.35 to about 2.15 g/cm 3 .
13. A method for making a gas and oil well proppant comprising a plurality of sintered, spherical pellets comprising preparing a composition comprising from about 20 to about 36 percent by weight of alumina fines and from about 63 to about 80 percent by weight of bauxite, wherein the alumina fines has an alumina content of about 99 percent by weight.
14. The method of claim 13 , wherein the composition comprises 36 percent by weight of alumina fines, 63 percent by weight of bauxite and 1 percent by weight of the at least one sintering aid.
15. The method of claim 13 , wherein the composition comprises 20 percent by weight of alumina fines and 80 percent by weight of bauxite.