Fluorspar-based filler and method for making the same
View Patent ↗A filler material that includes a metal fluoride compound which is coated with silica. The filler material can be used in various types of covering agents.
1. A method for forming a paint having improved hiding power and low sheen comprising:
a) providing a latex paint;
b) adding a pigment and a pigment extender to said latex paint, said pigment extender including a metal fluoride particle, said metal fluoride particle includes a composition of about 0.1-50 weight percent silica and about 50-99.9 weight percent metal fluoride.
2. The method as defined in claim 1 , wherein said metal fluoride particle includes a silica coated metal fluoride.
3. The method as defined in claim 2 , wherein said paint includes nepheline syenite, a weight ratio of metal fluoride particle to nepheline syenite is about 0.2-0.8:1.
4. The method as defined in claim 3 , wherein said metal fluoride particle includes calcium fluoride.
5. The method as defined in claim 2 , wherein said metal fluoride particle includes calcium fluoride.
6. The method as defined in claim 1 , wherein said paint includes nepheline syenite, a weight ratio of metal fluoride particle to nepheline syenite is about 0.2-0.8:1.
7. The method as defined in claim 1 , wherein said metal fluoride particle includes particles having a composition of about 60-80 weight percent metal fluoride and 20-40 weight percent silica.
8. The method as defined in claim 7 , wherein said metal fluoride particle has an average particle size of no greater than about 170 mesh.
9. The method as defined in claim 8 , wherein said latex paint includes a polymer having interpolymerized units that comprise units derived from styrene, methyl styrene, vinyl, or combinations thereof and units derived from one or more acrylates, methacrylates, acrylonitrile, and combinations thereof.
10. The method as defined in claim 9 , wherein said pigment includes titanium dioxide.
11. The method as defined in claim 10 , wherein said paint has an 85 sheen value of less than about 2.
12. The method as defined in claim 11 , wherein said metal fluoride particle is white and has a Tappi brightness value of about 84-91.
13. The method as defined in claim 12 , wherein said metal fluoride particle has average specific surface area of about 70-120 m 2 /g.
14. The method as defined in claim 13 , wherein a weight ratio of pigment extender to pigment in said paint is about 0.1-4:1.
15. The method as defined in claim 1 , wherein said metal fluoride particle has an average particle size of no greater than about 170 mesh.
16. The method as defined in claim 1 , wherein said latex paint includes a polymer having interpolymerized units that comprise units derived from styrene, methyl styrene, vinyl, or combinations thereof and units derived from one or more acrylates, methacrylates, acrylonitrile, and combinations thereof.
17. The method as defined in claim 1 , wherein said pigment includes titanium dioxide.
18. The method as defined in claim 1 , wherein said paint has an 85 sheen value of less than about 2.
19. The method as defined in claim 1 , wherein said metal fluoride particle is white and has a Tappi brightness value of about 84-91.
20. The method as defined in claim 1 , wherein said metal fluoride particle has average specific surface area of about 70-120 m 2 /g.
21. The method as defined in claim 1 , wherein a weight ratio of pigment extender to pigment in said paint is about 0.1-4:1.