Enhanced hexagonal ferrite material and methods of preparation and use thereof
View Patent ↗Embodiments and aspects of the present invention relate to an enhanced hexagonal ferrite magnetic material doped with an alkali metal. The material retains substantial magnetic permeability up to frequencies in the GHz range with low losses. The material may be used in high frequency applications in devices such as transformers, inductors, circulators, and absorbers.
1. An electrical component comprising Ba 3-y M x Co 2 Fe 24 O 41 where Ba is barium, M is at least one of potassium and rubidium, Co is cobalt, Fe is iron, O is oxygen, x is greater than zero and less than one, and y is greater than zero and less than or equal to x.
2. The electrical component of claim 1 wherein the Ba 3-y M x Co 2 Fe 24 O 41 has an average grain diameter in a range of between about 5 micrometers and about 1 millimeter.
3. The electrical component of claim 2 wherein the Ba 3-y M x Co 2 Fe 24 O 41 comprises a Z-type ferrite.
4. The electrical component of claim 3 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide an increased frequency corresponding to a peak of a real component of magnetic permeability of the Ba 3-y M x Co 2 Fe 24 O 41 relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
5. The electrical component of claim 4 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide an increased frequency corresponding to a peak of an imaginary component of magnetic permeability of the Ba 3-y M x Co 2 Fe 24 O 41 relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
6. The electrical component of claim 5 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide an increased a permeability to permittivity ratio μ r /∈ r of the Ba 3-y M x Co 2 Fe 24 O 41 at a frequency of at least one of about 0.5 GHz and about 1 GHz relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
7. The electrical component of claim 6 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide the Ba 3-y M x Co 2 Fe 24 O 41 with a permeability to permittivity ratio μ r /∈ r of greater than about 0.8 at a frequency of at least one of about 0.5 GHz and about 1 GHz.
8. The electrical component of claim 7 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the Ba 3-y M x Co 2 Fe 24 O 41 with a real component of relative magnetic permeability greater than about 10 at a frequency above 1 GHz.
9. The electrical component of claim 8 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the Ba 3-y M x Co 2 Fe 24 O 41 with a resonant frequency greater than 1 GHz.
10. The electrical component of claim 1 wherein the at least one of the potassium and rubidium is included in an amount sufficient to increase a frequency corresponding to a peak of a real component of magnetic permeability of the Ba 3-y M x Co 2 Fe 24 O 41 relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
11. The electrical component of claim 1 wherein an amount of the at least one of the potassium and rubidium is sufficient to provide an increased frequency corresponding to a peak of an imaginary component of magnetic permeability of the Ba 3-y M x Co 2 Fe 24 O 41 relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
12. The electrical component of claim 1 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide an increased permeability to permittivity ratio μ r /∈ r of the Ba 3-y M x Co 2 Fe 24 O 41 at a frequency of at least one of about 0.5 GHz and about 1 GHz relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
13. The electrical component of claim 12 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide the Ba 3-y M x Co 2 Fe 24 O 41 with a permeability to permittivity ratio μ r /∈ r of greater than about 0.8 at a frequency of at least one of about 0.5 GHz and about 1 GHz.
14. The electrical component of claim 1 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the Ba 3-y M x Co 2 Fe 24 O 41 with a real component of relative magnetic permeability at a frequency above 1 GHz greater than that of Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
15. The electrical component of claim 14 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the Ba 3-y M x Co 2 Fe 24 O 41 with a real component of relative magnetic permeability greater than about 10 at a frequency above 1 GHz.
16. The electrical component of claim 1 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the Ba 3-y M x Co 2 Fe 24 O 41 with a resonant frequency greater than that of Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
17. The electrical component of claim 1 wherein M further includes sodium.
18. The electrical component of claim 17 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the Ba 3-y M x Co 2 Fe 24 O 41 with a resonant frequency greater than 1 GHz.
19. The electrical component of claim 1 wherein the electrical component is a radio frequency ferrite circulator.
20. The electrical component of claim 19 wherein the radio frequency ferrite circulator is configured as an isolator.
21. The electrical component of claim 1 wherein the electrical component is any one of an inductor, a transformer, and an antenna.