Aqueous formaldehyde-free composition and fiberglass insulation including the same
View Patent ↗An aqueous composition that includes a) aqueous hydroxy functional, carboxy functional polymer including the reaction product of at least 5% by weight α,β-ethylenically unsaturated hydroxy monomer, at least 30% by weight ethylenically unsaturated carboxylic acid monomer, from 0% by weight to less than 50% by weight α,β-ethylenically unsaturated nonhydroxy functional, noncarboxy functional monomer, and chain transfer agent, and b) condensation accelerator, and articles that include a nonwoven web including glass fibers, and cured aqueous binder composition.
1. An aqueous composition comprising an aqueous water soluble hydroxy functional, carboxy functional polymer comprising the reaction product of
a.) at least 5% by weight α,β-ethylenically unsaturated hydroxy functional monomer,
b.) at least 60% by weight ethylenically unsaturated carboxylic acid monomer,
c.) 0% by weight to less than 35% by weight α,β-ethylenically unsaturated nonhydroxy functional, noncarboxy functional monomer, and
d.) chain transfer agent; and
wherein said aqueous composition has a pH less than about 7.
2. The aqueous composition of claim 1 , wherein said aqueous hydroxy functional carboxy functional polymer has a number average molecular weight no greater than 10,000.
3. The aqueous composition of claim 1 , wherein said aqueous composition has a pH from about 2 to about 4.
4. The aqueous composition of claim 1 , wherein said α,β-ethylenically unsaturated hydroxy functional monomer comprises 2-hydroxy ethyl acrylate.
5. The aqueous composition of claim 4 , wherein said ethylenically unsaturated carboxylic acid monomer comprises glacial acrylic acid.
6. The aqueous composition of claim 1 , wherein said ethylenically unsaturated carboxylic acid monomer comprises glacial acrylic acid.
7. The aqueous composition of claim 1 , wherein said aqueous hydroxy functional carboxy functional polymer is prepared from α,β-ethylenically unsaturated nonhydroxy functional, noncarboxy functional monomer, the amount of α,β-ethylenically unsaturated nonhydroxy functional, noncarboxy functional monomer being no greater than 35% by weight.
8. The aqueous composition of claim 1 , wherein said aqueous hydroxy functional carboxy functional polymer comprises from 20% by weight to 60% by weight solids.
9. The aqueous composition of claim 1 , wherein said aqueous hydroxy functional carboxy functional polymer has an acid number of at least 300 mg KOH/g dried polymer.
10. The aqueous composition of claim 1 , wherein said aqueous hydroxy functional, carboxy functional polymer comprises the reaction product of
a.) from 10% by weight to 40% by weight α,β-ethylenically unsaturated hydroxy functional monomer,
b.) from 60% by weight to 90% by weight ethylenically unsaturated carboxylic acid monomer, and
c.) chain transfer agent.
11. The aqueous composition of claim 1 , wherein said aqueous hydroxy functional, carboxy functional polymer comprises the reaction product of
a.) from 20% by weight to 40% by weight α,β-ethylenically unsaturated hydroxy functional monomer,
b.) from 60% by weight to 80% by weight ethylenically unsaturated carboxylic acid monomer, and
c.) chain transfer agent.
12. A method of making fiberglass insulation comprising:
a) contacting glass fibers with a binder composition comprising aqueous water soluble hydroxy functional carboxy functional polymer comprising the reaction product of
i.) at least 5% by weight α,β-ethylenically unsaturated hydroxy functional monomer,
ii.) at least 60% by weight ethylenically unsaturated carboxylic acid monomer,
iii.) less than 35% by weight nonhydroxy functional, noncarboxy functional monomer, and
iv.) chain transfer agent; and
wherein said binder composition has a pH less than about 7; and
b) curing said composition.
13. An aqueous fiberglass binder composition comprising an aqueous water soluble hydroxy functional, carboxy functional solution polymer consisting essentially of the reaction product of
i) at least 5% by weight α,β-ethylenically unsaturated hydroxy functional monomer,
ii) at least 60% by weight ethylenically unsaturated carboxylic acid monomer, and
iv) chain transfer agent; and
wherein said binder composition has a pH less than about 7.
14. The aqueous composition of claim 1 , wherein when said composition is employed in the Dry Tensile Strength Test Method, the cured treated paper exhibits a dry tensile strength of at least 5 pounds of force.
15. The aqueous composition of claim 1 , wherein when said composition is employed in the Wet Tensile Strength Test Method, the cured treated paper exhibits a wet tensile strength of at least 5 pounds of force.
16. The aqueous composition of claim 1 , wherein said aqueous hydroxy functional, carboxy functional solution polymer is free of α,β-ethylenically unsaturated nonhydroxy functional, noncarboxy functional monomer.
17. The an aqueous composition of claim 1 , wherein the chain transfer agent comprises sodium hypophosphite.
18. The aqueous composition of claim 1 , wherein the composition is free of transition metal catalyst.
19. The an aqueous composition of claim 1 , wherein the composition comprises no greater than 0.006% by weight transition metal catalyst based on solids in the composition.
20. The aqueous composition of claim 1 , wherein the aqueous water soluble hydroxy functional, carboxy functional polymer exhibits at least 99% monomer conversion.