ROLLING, SLIDING PART AND PROCESS FOR PRODUCING SAME
A rolling, sliding part is made from a bearing steel, and the rolling, sliding surface thereof has a surface layer portion which is 56 to 64 in Rockwell C hardness, up to 12 vol. % in retained austenite content and 4 to 6 degrees in the X-ray half value width of martensite. Even if made from a common bearing steel, the rolling, sliding part is reduced in the likelihood of developing a WEA or like fatigue structure, consequently exhibiting a prolonged rolling, sliding life for use under severe conditions involving a high temperature, high speed, high load or high vibration.
1 - 13 . (canceled)
14 . A process for producing a rolling, sliding part characterized by subjecting to a hardening treatment a worked part blank made from a bearing steel in a predetermined shape, subjecting the hardened blank to a tempering treatment at least twice and surface-hardening the resulting blank.
15 . A process for producing a rolling, sliding part according to claim 14 wherein the first tempering treatment is conducted at 150 to 170° C. and the final tempering treatment is conducted at 180 to 250° C.
16 . A process for producing a rolling, sliding part according to claim 14 wherein the tempering treatment is performed twice, and the first tempering treatment is conducted by holding the hardened blank at 150 to 170° C. for 60 to 120 minutes, and the second tempering treatment is conducted by holding the resulting blank at 180 to 250° C. for 60 to 120 minutes.
17 . A process for producing a rolling, sliding part according to claim 14 wherein a rolling body for use in a rolling bearing is produced from a worked part blank made from a high-carbon chromium bearing steel in a predetermined shape.
18 . A process for producing a rolling, sliding part according to claim 17 wherein JIS SUJ2 is used as the high-carbon chromium bearing steel.
19 . A process for producing a rolling, sliding part according to claim 14 wherein a worked part blank made from a high-carbon chromium bearing steel in a predetermined shape is used.
20 . A process for producing a rolling, sliding part according to claim 19 wherein JIS SUJ2 is used as the high-carbon chromium bearing steel.
21 . A rolling bearing comprising an inner and an outer ring and a rolling body wherein the rolling body is produced by a process according to claim 14 .
22 . A process for producing a rolling, sliding part made from a bearing steel, a rolling, sliding surface thereof having a surface layer portion which is 56 to 64 in Rockwell C hardness, up to 12 vol. % in retained austenite content and 4 to 6 degrees in the X-ray half value width of martensite,
characterized by subjecting to a hardening treatment a worked part blank made from a bearing steel in a predetermined shape, subjecting the hardened blank to a tempering treatment at least twice and surface-hardening the resulting blank
wherein, of the at least two tempering treatments, the first tempering treatment is conducted by holding the hardened blank at 150 to 170° C., and the final tempering treatment is conducted by holding the resulting blank at 180 to 250° C.
23 . A process for producing a rolling, sliding part according to claim 22 wherein JIS SUJ2 is used as the bearing steel.
24 . A process for producing a rolling, sliding part according to claim 22 wherein a rolling body for use in a rolling bearing is produced from a worked part blank formed in a predetermined shape.
25 . A process for producing a rolling, sliding part made from a bearing steel, a rolling, sliding surface thereof having a surface layer portion which is 56 to 64 in Rockwell C hardness, up to 12 vol. % in retained austenite content, 4 to 6 degrees in the X-ray half value width of martensite, and up to 1000 MPa in the absolute value of residual compressive stress,
characterized by subjecting to a hardening treatment a worked part blank made from a bearing steel in a predetermined shape, subjecting the hardened blank to a tempering treatment at least twice and surface-hardening the resulting blank
wherein, of the at least two tempering treatments, the first tempering treatment is conducted by holding the hardened blank at 150 to 170° C., and the final tempering treatment is conducted by holding the resulting blank at 180 to 250° C.
26 . A process for producing a rolling, sliding part according to claim 25 wherein JIS SUJ2 is used as the bearing steel.
27 . A process for producing a rolling, sliding part according to claim 25 wherein a rolling body for use in a rolling bearing is produced from a worked part blank formed in a predetermined shape.
28 . A rolling bearing comprising an inner and an outer ring and a rolling body wherein the rolling body is produced by a process according to claim 22 .
29 . A rolling bearing comprising an inner and an outer ring and a rolling body wherein the rolling body is produced by a process according to claim 25 .