Polyisocyanate mixtures, processes for preparing the same and uses therefor
View Patent ↗Polyisocyanate mixtures, their preparation by reacting aromatic polyisocyanate mixtures and nitrogen-containing polyetherol mixtures, and their use as an isocyanate component for the preparation of moisture-curing adhesives, said polyisocyanate mixtures comprising: (A) 15 to 35 wt. % of diphenylmethane diisocyanate with 2 aromatic rings; (3) 10 to 30 wt. % of polymeric diphenylmethane diisocyanate with 3 or more aromatic rings; and (C) 40 to 75 wt. % of an isocyanate-functional polyurethane; wherein the polyisocyanate mixture has an isocyanate content of 12 to 20 wt. %, an isocyanate functionality of >2.4, a viscosity of <10,000 mPa·s at 25° C., and a shear rate of 80 l/s.
1. A polyisocyanate mixture comprising:
(A) 15 to 35 wt. % of diphenylmethane diisocyanate with 2 aromatic rings;
(B) 10 to 30 wt. % of polymeric diphenylmethane diisocyanate with 3 or more aromatic rings; and
(C) 40 to 75 wt. % of an isocyanate-functional polyurethane component;
wherein the polyisocyanate mixture has an isocyanate content of 12 to 20 wt. %, an isocyanate functionality of >2.4, a viscosity of <10,000 mPa·s at 25° C., and a shear rate of 80 l/s, and wherein the isocyanate-functional polyurethane component comprises a mixture of prepolymers prepared by reacting:
(i) a first mixture comprising:
(a) at least one first aromatic polyisocyanate reactant mixture comprising diphenylmethane diisocyanate and having >38% of its isocyanate groups in the 4,4′ position and having 0 to 60% of its isocyanate groups in the 2,4′ position, 0 to 2% of its isocyanate groups in the 2,2′-position, an isocyanate content of >33 wt. % and a functionality of 2.0; and
(b) at least one second aromatic polyisocyanate reactant mixture comprising diphenylmethane diisocyanate and having <50% of its isocyanate groups in the 4,4′ position, 10 to 15% of its isocyanate groups in the 2,4′ position, and 0.1 to 5% of its isocyanate groups in the 2,2′ position, an isocyanate content of 30 to 33 wt. % and a functionality of >2.0;
with (ii) a second mixture comprising:
(c) at least one amino group-free polyether based on propylene oxide having an OH number of 40 to 80 mg KOH/g and a functionality of at least 2.0; and
(d) at least one amino group-containing polyether based on propylene oxide having an OH number of 40 to 80 mg KOH/g, a functionality of 4.0 and an amine content of 0.499 to 0.998 wt. %.
2. The polyisocyanate mixture according to claim 1 , wherein the polyisocyanate mixture has an isocyanate content of 13 to 19 wt. %, an isocyanate functionality of >2.4, a viscosity of <9,000 mPa·s at 25° C., and a shear rate of 80 l/s.
3. The polyisocyanate mixture according to claim 1 , wherein the polyisocyanate mixture has an isocyanate content of 14 to 18 wt. %, an isocyanate functionality of >2.6, a viscosity of <7,000 mPa·s at 25° C., and a shear rate of 80 l/s.
4. An adhesive formulation comprising the polyisocyanate mixture according to claim 1 .
5. The adhesive formulation according to claim 4 , wherein the formulation comprises a moisture-curing adhesive.
6. An article comprising a substrate having a coating disposed on a surface of the substrate, wherein the coating comprises the polyisocyanate mixture according to claim 1 .
7. An article comprising two substrates bonded to one another with an adhesive disposed between the two substrates, wherein the adhesive comprises the polyisocyanate mixture according to claim 1 .
8. A method comprising; (a) providing a substrate having a surface; and (b) applying a formulation comprising the polyisocyanate mixture according to claim 1 to at least a portion of the surface.