Aluminum alloy products having improved property combinations and method for artificially aging same
View Patent ↗Aluminum alloy products about 4 inches thick or less that possesses the ability to achieve, when solution heat treated, quenched, and artificially aged, and in parts made from the products, an improved combination of strength, fracture toughness and corrosion resistance, the alloy consisting essentially of: about 6.8 to about 8.5 wt. % Zn, about 1.5 to about 2.00 wt. % Mg, about 1.75 to about 2.3 wt. % Cu; about 0.05 to about 0.3 wt. % Zr, less than about 0.1 wt. % Mn, less than about 0.05 wt. % Cr, the balance Al, incidental elements and impurities and a method for making same. The instantly disclosed alloys are useful in making structural members for commercial airplanes including, but not limited to, upper wing skins and stringers, spar caps, spar webs and ribs of either built-up or integral construction.
1. A plate comprising an aluminum alloy, wherein the aluminum alloy consists essentially of 6.8-8.5 wt. % Zn, 1.75-2.3 wt. % Cu, 1.5-1.84 wt. % Mg, and up to 0.25 wt. % of at least one of Zr, Hf, Sc, Mn, and V, the balance being aluminum, incidental elements and impurities;
wherein the plate has a thickness of not greater than 2.00 inches;
wherein the plate has strength-to-toughness relationship that satisfies the expression:
FT_LT≧−4.0*(TYS_L)+453;
wherein the plate has a TYS_L of at least 80 ksi;
wherein the plate has a FT_LT of at least 100 ksi√inch;
wherein TYS_L is the L tensile yield strength of the plate in ksi as measured in accordance with ASTM Standard E8 and ASTM B557;
wherein FT_LT is the L-T plane stress fracture toughness (K app ) of the plate in ksi√inch as measured in accordance with ASTM Standard E561 and B646 on a center-cracked aluminum alloy specimen taken from the T/2 location of the plate, wherein the specimen has a width of 16 inches, a thickness of 0.25 inch and a initial fatigue pre-crack length of 4 inches.
2. The plate of claim 1 , wherein, the amount of Mg in the aluminum alloy is in the range of 1.6 to 1.75 wt. %.
3. A plate comprising an aluminum alloy, wherein the aluminum alloy consists essentially of 6.8-8.5 wt. % Zn, 1.75-2.3 wt. % Cu, 1.5-1.84 wt. % Mg, and up to 0.25 wt. % of at least one of Zr, Hf, Sc, Mn, and V, the balance being aluminum, incidental elements and impurities;
wherein the plate has a thickness of not greater than 2.00 inches;
wherein the plate has a strength-to-toughness relationship that satisfies the expression:
FT-KIC≧−2.3*(TYS_L)+229;
wherein the plate has a TYS_L of at least 74 ksi;
wherein the plate has a FT-KIC of at least 30 ksi√inch;
wherein TYS_L is the L tensile yield strength of the plate in ksi as measured in accordance with ASTM Standard E8 and ASTM B557;
wherein FT-KIC is the L-T plane strain fracture toughness of the plate in ksi√inch as measured in accordance with ASTM E399; and
wherein the fracture toughness specimens are of full plate thickness.
4. The plate of claim 3 , wherein the amount of Mg in the aluminum alloy is in the range of 1.6 to 1.75 wt. %.
5. A plate comprising an aluminum alloy, wherein the aluminum alloy consists essentially 6.8-8.5 wt. % Zn, 1.75-2.3 wt. % Cu, 1.5-1.84 wt. % Mg, and up to 0.25 wt. % of at least one of Zr, Sc, Mn, and V, the balance being aluminum incidental elements and impurities;
wherein the plate has a thickness of from 2.00 inches to 3.25 inches,
wherein the plate has a strength-to-toughness relationship that satisfies the expression:
FT_TL≧−1.0*(TYS_LT)+98,
wherein the plate has a TYS_LT of at least 72 ksi,
wherein the plate has a FT_TL of at least 22 ksi√inch,
wherein TYS_LT is the LT tensile yield strength of the plate in ksi as measured in accordance with ASTM Standard E8 and ASTM B557, and
where FT_TL is the T-L plane strain fracture toughness of the plate in ksi√inch as measured in accordance with ASTM E399 at the T/2 location of the plate.
6. The plate of claim 5 , wherein the FT_TL is at least 24.5 ksi√inch.
7. The plate of claim 6 , wherein the TYS_LT is at least 76 ksi.
8. The plate of claim 5 , wherein the plate has a strength-to-toughness relationship that satisfies the expression:
FT_SL≧−1.1*(TYS_ST)+99;
wherein the plate has a TYS_ST of at least 69 ksi;
wherein the plate has a FT_SL of at least 22 ksi√inch;
wherein TYS_ST is the ST tensile yield strength of the plate in ksi as measured in accordance with ASTM Standard E8 and ASTM B557; and
wherein FT_SL is the S-L plane strain fracture toughness of the plate in ksi√inch as T/2 measured in accordance with ASTM E399 at the T/2 location of the plate.
9. The plate of claim 8 , wherein the FT_SL is at least 25 ksi√inch.
10. The plate of claim 9 , wherein the TYS_ST is at least 71 ksi.
11. The plate of claim 5 , wherein the plate consistently passes alternate immersion stress corrosion cracking resistance tests at a stress level of at least about 25 ksi as measured in accordance with ASTM standards G44, G47 and G49 on test specimens taken at the mid-thickness (T/2) in the ST direction for a period of at least 30 days.
12. The plate of claim 11 , wherein the plate consistently passes seacoast environment stress corrosion cracking resistance tests at the stress level as measured on test specimens taken at the mid-thickness (T/2) in the ST direction for a period of at least 180 days.
13. The plate of claim 12 , wherein the stress level is at least about 35 ksi for at least one of the alternate immersion stress corrosion cracking resistance tests and the seacoast environment stress corrosion cracking resistance tests.
14. A plate comprising an aluminum alloy, wherein the aluminum alloy consisting essentially 6.8-8.5 wt. % Zn, 1.75-2.3 wt. % Cu, 1.5-1.84 wt. % Mg, and up to 0.25 wt. % of at least one of Zr, Hf, Sc, Mn, and V, the balance being aluminum incidental elements and impurities;
wherein the plate has a thickness of from 2.75 inches to 4 inches;
wherein the plate has a strength-to-toughness relationship that satisfies the expression:
FT_TL≧−1.0*(TYS_LT)+98;
wherein the plate has a TYS_LT of at least 71 ksi;
wherein the plate has a FT_TL of at least 21 ksi√inch;
wherein TYS_LT is the LT tensile yield strength of the plate in ksi as measured in accordance with ASTM Standard E8 and ASTM B557; and
wherein FT_TL is the T-L plane strain fracture toughness of the plate in ksi√inch as measured in accordance with ASTM E399 at the T/2 location of the plate.
15. The plate of claim 14 , wherein the FT_TL, is at least 23 ksi√inch.
16. The plate of claim 15 , wherein the TYS_LT is at least 74 ksi.
17. The plate of claim 14 , wherein the plate has a strength-to-toughness relationship that satisfies the expression:
FT_SL≧−1.1*(TYS_ST)+99;
wherein the plate has a TYS_ST of at least 66 ksi;
wherein the plate has a FT_SL of at least 20 ksi√inch;
wherein TYS_ST is the ST tensile yield strength of the plate in ksi as measured in accordance with ASTM Standard E8 and ASTM B557; and
wherein FT_SL is the S-L plane strain fracture toughness of the plate in ksi√inch as measured in accordance with ASTM E399 at the T/2 location of the plate.
18. The plate of claim 17 , wherein the FT_SL is at least 23 ksi√inch.
19. The plate of claim 18 , wherein the TYS_ST is at least 69 ksi.
20. The plate of claim 14 , wherein the plate consistently passes alternate immersion stress corrosion cracking resistance tests at a stress level of at least about 25 ksi as measured in accordance with ASTM standards G44, G47 and G49 on test specimens taken at the mid-thickness (T/2) in the ST direction for a period of at least 30 days.
21. The plate of claim 20 , wherein the plate consistently passes seacoast environment stress corrosion cracking resistance tests at the stress level as measured on test specimens taken at the mid-thickness (T/2) in the ST direction for a period of at least 180 days.
22. The plate of claim 21 , wherein the stress level is at least about 35 ksi for at least one of the alternate immersion stress corrosion cracking resistance tests and the seacoast environment stress corrosion cracking resistance tests.