Pigment dispersion, precursor of ink for UV-curing type ink-jet recording, method of ink-jet recording, printed matter, and method of manufacturing pigment dispersion
View Patent ↗There is provided a pigment dispersion comprising at least one resin-coated pigment comprising a resin and a pigment, and having an average particle diameter of 250 nm or less, and a dispersion medium containing as a major component a cation polymeric compound having a viscosity of 30 mPa·s or less at a temperature of 25° C. and a boiling point of 150° C. or more at 1 atm. The pigment is incorporated in the pigment dispersion at a ratio ranging from 3 to 41% by weight based on a total weight of the dispersion medium, and the resin is incorporated in the resin-coated pigment at a ratio ranging from 5 to 37% by weight based on the weight of the pigment.
1. A pigment dispersion comprising:
at least one resin-coated pigment comprising a resin and a pigment, and having an average particle diameter of 250 nm or less; and
a dispersion medium having a viscosity of 30 mPa·s or less at a temperature of 25° C. and a boiling point of 150° C. or more at 1 atm, the dispersion medium containing as a major component a cation polymeric compound selected from a group consisting of: a compound having a molecular weight of not more than 1000 and comprising a cyclic ether moiety; an acrylic compound having an epoxy, oxetane, or oxolane group; a vinyl compound having an epoxy, oxetane, or oxolane group; a carbonate compound; a low molecular melamine compound; a vinyl ether; a vinyl carbazole; a styrene derivative; an alpha-methylstyrene derivative; a vinyl alcohol ester; an ester of vinyl alcohol having an acryl or a methacryl group; and a monomer having a cation polymerizable vinyl bond;
wherein a mixing ratio of the pigment is confined within the range of 3 to 41% by weight based on a total weight of the dispersion medium, and a ratio of the resin in the resin-coated pigment is confined within the range of 5 to 37% by weight based on the weight of the pigment.
2. The pigment dispersion according to claim 1 , wherein the pigment is carbon black, the content of which ranging from 3 to 28% by weight based on a total weight of the dispersion medium, and the content of the resin in the resin-coated pigment is confined within the range of 10 to 30% by weight based on the pigment.
3. The pigment dispersion according to claim 1 , wherein the pigment is benzimidazolone-based yellow pigment, the content of which ranging from 3 to 28% by weight based on a total weight of the dispersion medium, and the content of the resin in the resin-coated pigment is confined within the range of 15 to 39% by weight based on the pigment.
4. The pigment dispersion according to claim 1 , wherein the pigment is phthalocyanine-based cyan pigment, the content of which ranging from 3 to 28% by weight based on a total weight of the dispersion medium, and the content of the resin in the resin-coated pigment is confined within the range of 10 to 30% by weight based on the pigment.
5. The pigment dispersion according to claim 1 , wherein the pigment is quinacridone-based magenta pigment, the content of which ranging from 3 to 28% by weight based on a total weight of the dispersion medium, and the content of the resin in the resin-coated pigment is confined within the range of 20 to 39% by weight based on the pigment.
6. The pigment dispersion according to claim 1 , wherein the dispersion medium further comprises not more than 5% by weight of a ketone-based organic solvent based on a total weight of the dispersion medium.
7. The pigment dispersion according to claim 1 , further comprising at least one of a photo-acid generating agent and a basic compound.
8. The pigment dispersion according to claim 1 , wherein the dispersion medium includes limonene diepoxide.
9. The pigment dispersion according to claim 1 , wherein the dispersion medium includes neopentyl glycol diglycidyl ether and/or di[1-ethyl(3-oxetanyl)]methyl ether.
10. The pigment dispersion according to claim 7 , wherein the mixing ratio of the basic compound is less than 1% by weight.
11. The pigment dispersion according to claim 1 , wherein the dispersion medium includes cyclohexane di-vinyl ether.