Photocatalytic methods for preparation of electrocatalyst materials
View Patent ↗The invention relates to methods of preparing metal particles on a support material, including platinum-containing nanoparticles on a carbon support. Such materials can be used as electrocatalysts, for example as improved electrocatalysts in proton exchange membrane fuel cells (PEM-FCs).
1. A method for making an electrocatalyst, the method comprising:
providing a first mixture, the first mixture including a photocatalyst, a first reductant, and a first metal compound;
illuminating the first mixture so as to form metal seeds by reduction of the metal compound;
adding the metal seeds to a separate second mixture, the separate second mixture including a support material,
supporting the metal seeds on the support material; and
adding a second reductant and a second metal compound to the resulting separate second mixture containing the metal seeds supported on the support material to form the electrocatalyst, the support material being electron conducting.
2. The method of claim 1 , wherein the photocatalyst is an organometallic or free base porphyrin compound.
3. The method of claim 1 , wherein the photocatalyst is a metal porphyrin.
4. The method of claim 1 , wherein the photocatalyst is a tin porphyrin.
5. The method of claim 4 , wherein the tin porphyrin is meso-tetra(sulfonato-4-phenyl) porphyrin (SnTPPS4).
6. The method of claim 5 , wherein the meso-tetra(sulfonato-4-phenyl) porphyrin (SnTPPS4) is negatively charged and stabilizes the metal seeds by serving as a capping agent.
7. The method of claim 5 , wherein the meso-tetra(sulfonato-4-phenyl) porphyrin (SnTPPS4) interacts with the metal seeds providing separation between the metals seeds.
8. The method of claim 1 , wherein the first mixture includes at least one metal compound selected from a group consisting of platinum compounds, cobalt compounds, palladium compounds, iron compounds, and nickel compounds.
9. The method of claim 1 , wherein the metal seeds are platinum-containing seeds.
10. The method of claim 9 , wherein the metal particles have a median diameter between 1 and 20 nm.
11. The method of claim 1 , wherein the second reductant is the same as the first reductant.
12. The method of claim 1 , wherein the second metal compound is the same as the first metal compound.
13. The method of claim 1 , wherein the reductant is selected from the group of reductants consisting of ascorbic acid and hydroquinone.
14. The method of claim 1 , wherein the support material comprises carbon.
15. The method of claim 1 , wherein supporting the metal seeds on the support material comprises adding the metal seeds to a suspension of the support material.
16. The method of claim 1 , wherein the suspension of the support material with the metal seeds added thereto are subjected to sonication.
17. The method of claim 1 , wherein illuminating the mixture comprises exposing the mixture to visible or UV light.
18. The method of claim 1 , further comprising pyrolyzing the electrocatalyst to convert organic components to additional carbon support material.
19. The method of claim 1 , wherein adding the second reductant and the second metal compound to the resulting separate second mixture containing the metal seeds supported on the support material to form the electrocatalyst with a plurality of metal particles on the electron conducting support material, the plurality of metal particles having a median diameter between 1 and 20 nm.