High voltage niobium oxides and capacitors containing same
View Patent ↗Nb 1-x Ta x O powder wherein x is 0.1 to 0.5 is described. Further, this powder, as well as niobium suboxide powders, can be doped with at least one dopant oxide. Pressed bodies of the powder, sintered bodies, capacitor anodes, and capacitors are also described.
1. A niobium suboxide powder having the formula Nb x O y that is doped with at least one dopant oxide, wherein x is less than 2 and y is less than 2.5× wherein said dopant oxide is an oxide of Y, Si, Mn, Al, or Ce, or any combination thereof, and said dopant oxide has a cation valency of +2 or higher, and wherein said dopant oxide is present in an amount of from 0.25% by weight to 2.5% by weight, based on the overall weight of the powder.
2. The niobium suboxide powder of claim 1 , wherein said dopant oxide has an ionic size that is within 10% of an ionic size for niobium.
3. A capacitor anode comprising a sintered pressed body comprising the niobium suboxide powder of claim 1 .
4. The capacitor anode of claim 3 , wherein said capacitor anode further comprises a dielectric layer without any field-induced crystallization within said dielectric layer.
5. The capacitor anode of claim 3 , wherein said capacitor anode is formed with a formation voltage of from 60 volts to 75 volts with a pressed density of 3.0 g/cc or higher, and sintered at a temperature of from 1000° C. to 1400° C. for 10 minutes or more at a formation temperature of 90° C.
6. The capacitor anode of claim 5 , wherein said anode has a cumulative volume of pores of greater than 1 micron diameter of 0.010 mL/g or higher.
7. The niobium suboxide powder of claim 1 , wherein said dopant oxide is Y 2 O 3 , SiO 2 , Mn 3 O 4 , Mn 2 O 3 , Al 2 O 3 , CeO 2 , or any combination thereof.
8. The niobium suboxide powder of claim 1 , wherein said dopant oxide is Y 2 O 3 , SiO 2 , Mn 2 O 3 , or any combination thereof.
9. The niobium suboxide powder of claim 1 , wherein said dopant oxide is Y 2 O 3 , SiO 2 , or any combination thereof.
10. The niobium suboxide powder of claim 1 , wherein said dopant oxide is Y 2 O 3 .