Method for processing and analyzing contaminated mixed waste plastics to produce reformulated, blended feed materials having a desired plastic content
View Patent ↗A method for reformulating reclaimed, contaminated mixed waste plastics into useful articles wherein a plurality of batches of the mixed waste plastics are preprocessed to produce substantially homogeneous mixtures of a desired particle size range that are characterized according to their respective apparent densities, and are thereafter blended to produce a mixed plastic feed material having a plastic content predetermined to be desirable for reprocessing into at least one of such useful articles.
1. A method for preparing a reformulated plastic-containing feed material wherein the reformulated plastic-containing feed material is blended from a plurality of batches of contaminated, reclaimed mixed waste plastic comprising gross contaminants, filler materials, and a major portion of linear short chain branched polyethylene (LSCBPE), the method comprising:
preprocessing a plurality of different batches of contaminated, reclaimed mixed waste plastic by removing the gross contaminants, shredding the resultant product, densifying the shredded mixed waste plastic to a bulk density of at least about 16 pounds per cubic foot, and pulverizing the densified mixed waste plastic to a predetermined maximum particle size;
selecting a sample from each of the plurality of batches of preprocessed mixed waste plastic;
further reducing the particle size of the sample to obtain a more uniform particle size distribution;
injection molding a substantially homogeneous composition from the mixed waste plastic within each sample;
analyzing at least a portion of each injection molded composition to determine from a graph of the heat of melting versus temperature the heat flux required to melt the LSCBPE in the analyzed portion of the injection molded composition;
calculating the LSCBPE content of the sample;
calculating a reformulated blend including mixed waste plastic from at least some of the plurality of batches of mixed waste plastic based upon the LSCBPE content of the injection molded compositions; and
blending a quantity of mixed waste plastic from the at least some of the plurality of batches of mixed waste plastic according to the calculated reformulated blend to produce a reformulated plastic-containing feed material having a desired LSCBPE content.
2. The method of claim 1 wherein the particle size of the sample is further reduced to a size that will pass through a 2 mm screen.
3. The method of claim 1 wherein the reformulated blend is calculated using an algorithm.
4. The method of claim 1 wherein the reformulated blend is calculated to include an amount of virgin polymeric resin.
5. The method of claim 1 wherein the reformulated plastic-containing feed material is useful for making composite wood and plastic products.
6. The method of claim 1 wherein the predetermined maximum particle size is about −10 mesh.
7. The method of claim 1 wherein each selected sample is milled prior to injection molding.
8. The method of claim 1 wherein an apparent density of each injection molded composition is determined from measurement of the heat flux required to melt a test sample taken from the injection molded composition as a function of temperature.
9. The method of claim 8 wherein the test sample is analyzed using a differential scanning calorimeter.
10. The method of claim 1 wherein a portion of the injection molded composition is analyzed to determine a level of contaminants.
11. The method of claim 1 wherein a portion of the injection molded composition is analyzed to determine a level of color.
12. The method of claim 1 wherein the blending is done under conditions that promote thorough mixing.
13. A method for preparing a reformulated plastic-containing feed material wherein the reformulated plastic-containing feed material is blended from a plurality of batches of contaminated, reclaimed mixed waste plastic comprising gross contaminants, filler materials, and a major portion of long chain branched polyethylene (LCBPE), the method comprising:
preprocessing a plurality of different batches of contaminated, reclaimed mixed waste plastic by removing the gross contaminants, shredding the resultant product, densifying the shredded mixed waste plastic to a bulk density of at least about 16 pounds per cubic foot, and pulverizing the densified mixed waste plastic to a predetermined maximum particle size;
selecting a sample from each of the plurality of batches of preprocessed mixed waste plastic;
further reducing the particle size of the sample to obtain a more uniform particle size distribution;
injection molding a substantially homogeneous composition from the mixed waste plastic within each sample;
analyzing at least a portion of each injection molded composition to determine from a graph of the heat of melting versus temperature the heat flux required to melt the LCBPE in the analyzed portion of the injection molded composition;
calculating the LCBPE content of the sample;
calculating a reformulated blend including mixed waste plastic from at least some of the plurality of batches of mixed waste plastic based upon the LCBPE content of the injection molded compositions; and
blending a quantity of mixed waste plastic from the at least some of the plurality of batches of mixed waste plastic according to the calculated reformulated blend to produce a reformulated plastic-containing feed material having a desired LCBPE content.
14. The method of claim 13 wherein the particle size of the sample is further reduced to a size that will pass through a 2 mm screen.
15. The method of claim 13 wherein the reformulated blend is calculated using an algorithm.
16. The method of claim 13 wherein the reformulated blend is calculated to include an amount of virgin polymeric resin.
17. The method of claim 13 wherein the reformulated plastic-containing feed material is useful for making composite wood and plastic products.
18. The method of claim 13 wherein the predetermined maximum particle size is about −10 mesh.
19. The method of claim 13 wherein each selected sample is milled prior to injection molding.
20. The method of claim 19 wherein an apparent density of each injection molded composition is determined from measurement of the heat flux required to melt a test sample taken from the injection molded composition as a function of temperature.
21. The method of claim 20 wherein the test sample is analyzed using a differential scanning calorimeter.
22. The method of claim 13 wherein a portion of the injection molded composition is analyzed to determine a level of contaminants.
23. The method of claim 13 wherein a portion of the injection molded composition is analyzed to determine a level of color.
24. The method of claim 13 wherein the blending is done under conditions that promote thorough mixing.