Two-part polyurethane adhesives for structural finger joints and method therefor
View Patent ↗One aspect of the present invention is an adhesive composition formed from two packs. One pack includes an isocyanate-functional prepolymer formed by reacting a polyisocyanate with an alcohol (e.g., polyol). The isocyanate equivalents from the polyisocyanate exceed the hydroxyl equivalents from the alcohol. The second pack is an aqueous polymer emulsion. These two packs are combined to form the novel adhesive composition. Another aspect of the invention is a method for joining together two surfaces of wood products by application of an adhesive thereto. The first step in this method is to mist with water the wood product surfaces to be joined. An adhesive composition then is applied to the misted wood product surfaces. Alternatively, the water misting can be replaced with an aqueous emulsion being part of the adhesive composition. Finally, the adhesive composition is cured.
1. Method for joining together two surfaces of wood products having a moisture content of less than about 10% by weight by application of an aqueous adhesive thereto, which comprises the steps of:
(a) misting the wood product surfaces to be joined with water;
(b) applying to said aqueous adhesive composition to said misted wood product surfaces; and
(c) curing said adhesive composition.
2. The method of claim 1 , wherein said aqueous adhesive composition is applied to said misted wood product surfaces within about 5 minutes after said misting.
3. The method of claim 1 , wherein said surfaces are misted to saturation.
4. The method of claim 1 , wherein said adhesive composition comprises:
(a) an isocyanate-functional prepolymer formed by reacting a polyisocyanate with an alcohol, where the isocyanate equivalents from the polyisocyanate exceeds the hydroxyl equivalents from the alcohol; and
(b) an aqueous polymer emulsion, the weight ratio of (a) to (b) ranging from about 95/5 to about 60/40.
5. The method of claim 1 , wherein said adhesive has been cured by heat or radio frequency (RF) curing.
6. The method of claim 4 , wherein said alcohol is selected from one or more of acrylates, esters, vinyls, castor oils, or polymers, containing active alcohol groups.
7. The method of claim 6 , wherein said alcohol is selected from one or more of aliphatic and aromatic polyether polyols optionally alkylated, or caprolactone-based polyols.
8. The method of claim 7 , wherein said alcohol is a block polyethylene or polypropylene oxide homo- or co-polymer ranging in molecular weight from about 300 to about 3,000.
9. The method of claim 4 , wherein said isocyanate-terminated prepolymer is made from an isocyanate component selected from hexamethylene diisocyanate, toluene diisocyanate (TDI), diphenylmethane diisocyanate (MDI), m- and p-phenylene diisocyanates, bitolylene diisocyanate, cyclohexane diisocyanate (CHDI), bis-(isocyanatomethyl)cyclohexane (H 6 XDI), dicyclohexylmethane diisocyanate (H 12 MDI), dimer acid diisocyanate (DDI), trimethyl hexamethylene diisocyanate, lysine diisocyanate and its methyl ester, isophorone diisocyanate, methyl cyclohexane diisocyanate, 1,5-napthalene diisocyanate, xylylene and xylene diisocyanate and methyl derivatives thereof, polymethylene polyphenyl isocyanates, chlorophenylene-2,4-diisocyanate, polyphenylene diisocyanates, isophorone diisocyanate (IPDI), hydrogenated methylene diphenyl isocyanate (HMDI), tetramethyl xylene diisocyanate (TMXDI), hexamethylene diisocyanate (HDI), or oligomers thereof, and mixtures thereof.
10. The method of claim 4 , wherein said isocyanate prepolymer contains a defoamer and an inhibitor.
11. The method of claim 4 , wherein the weight ratio of said isocyanate-functional prepolymer to said aqueous polymer emulsion ranges from about 90/10 to about 70/30.
12. The method of claim 4 , wherein said aqueous polymer emulsion is one or more of acrylic emulsions, vinyl emulsions, styrene-butadiene polymeric emulsion latices, polyvinyl alcohol emulsions, polyurethane dispersions, polyvinyl acetate-ethylene copolymer emulsions, or carboxylated acrylic latexes.