Frit seal material, lamp with frit seal, and method for sealing a high intensity discharge lamp
View Patent ↗A high intensity discharge lamp includes an arc tube with a chemical fill, capillaries extended from the arc tube, electrodes fed through the capillaries into the arc tube, and a frit seal that seals the capillaries, where the frit seal includes silica (SiO 2 ) in a range of more than 0 wt % to less than 5 wt %, alumina (Al 2 O 3 ), and one of dysprosia (Dy 2 O 3 ) and yttrium oxide (Y 2 O 3 ). This frit seal material can withstand a higher operating temperature so that the length of the capillaries can be reduced compared to those sealed with conventional frit seal material.
1. A material for sealing a ceramic body, the material consisting essentially of silica (SiO 2 ) in a range of more than 0 wt % to less than 5 wt %, alumina (Al 2 O 3 ), and one of dysprosia (Dy 2 O 3 ) or yttrium oxide (Y 2 O 3 ), wherein the material has a composition close to either a Al 2 O 3 /Dy 2 O 3 eutectic composition having a melting point of 1762° C. or a Al 2 O 3 /Y 2 O 3 eutectic composition having a melting point of 1826° C.
2. The material of claim 1 , with 2.9 wt % silica, 50.7 wt % alumina, and 46.4 wt % dysprosia.
3. The material of claim 1 , with 4.8 wt % silica, 49.7 wt % alumina, and 45.5 wt % dysprosia.
4. The material of claim 1 , with 2.9 wt % silica, 64.6 wt % alumina, and 32.5 wt % yttrium oxide.
5. The material of claim 1 , with 4.8 wt % silica, 63.6 wt % alumina, and 31.6 wt % yttrium oxide.
6. A high intensity discharge lamp comprising:
an arc tube with a chemical fill;
capillaries extended from the arc tube;
electrodes fed through the capillaries into the arc tube; and
a frit seal that seals the capillaries, the frit seal consisting essentially of silica (SiO 2 ) in a range of more than 0 wt % to less than 5 wt %, alumina (Al 2 O 3 ), and one of dysprosia (Dy 2 O 3 ) or yttrium oxide (Y 2 O 3 ), wherein the frit seal has a composition close to either a Al 2 O 3 /Dy 2 O 3 eutectic composition having a melting point of 1762° C. or a Al 2 O 3 /Y 2 O 3 eutectic composition having a melting point of 1826° C.
7. The lamp of claim 6 , wherein the capillaries have a length that is less than a diameter of the arc tube.
8. The lamp of claim 6 , wherein the frit seal has 2.9 wt % silica, 50.7 wt % alumina, and 46.4 wt % dysprosia.
9. The lamp of claim 6 , wherein the frit seal has 4.8 wt % silica, 49.7 wt % alumina, and 45.5 wt % dysprosia.
10. The lamp of claim 6 , wherein the frit seal has 2.9 wt % silica, 64.6 wt % alumina, and 32.5 wt % yttrium oxide.
11. The lamp of claim 6 , wherein the frit seal has 4.8 wt % silica, 63.6 wt % alumina, and 31.6 wt % yttrium oxide.
12. A method making a frit seal for a high intensity discharge lamp, comprising the steps of:
mixing silica (SiO 2 ) in a range of more than 0 wt % to less than 5 wt %, alumina (Al 2 O 3 ), and one of dysprosia (Dy 2 O 3 ) or yttrium oxide (Y 2 O 3 ) to form a mixture, wherein the mixture has a composition close to either a Al 2 O 3 /Dy 2 O 3 eutectic composition having a melting point of 1762° C. or a Al 2 O 3 /Y 2 O 3 eutectic composition having a melting point of 1826° C.,
adding a binder to the mixture;
pressing the mixture and binder into rings; and
sintering the rings to remove the binder.
13. The method of claim 12 , further comprising the steps of mounting the sintered rings on electrodes at ends of capillaries that are attached to an arc tube with a chemical fill, and melting the sintered rings to seal the capillaries.