Precipitated iron catalyst for hydrogenation of carbon monoxide
View Patent ↗A method of producing an iron catalyst for catalyzing the hydrogenation of carbon monoxide is disclosed. The method comprises using a reduced amount of acid for iron dissolution compared to certain previous methods. The resulting acidic iron mixture is heated without boiling to obtain a nitrate solution having a Fe 2+ :Fe 3+ ratio in the range of about 0.01%:99.99% to about 100%:0% (wt:wt). Iron phases are precipitated at a lower temperature compared to certain previous methods. The recovered catalyst precursor is dried and sized to form particles having a size distribution between 10 microns and 100 microns. In embodiments, the Fe 2+ :Fe 3+ ratio in the nitric acid solution may be in the range of from about 3%:97% to about 30%:70% (wt:wt) and the calcined catalyst may comprise a maghemite:hematite ratio of about 1%:99% to about 70%:30%.
1. A catalyst for hydrogenating carbon monoxide, the catalyst comprising iron, copper and potassium, wherein the catalyst comprises one part by weight copper per 100 parts iron and from 0.5 to 1.5 parts by weight potassium per 100 parts iron, and wherein the iron in the catalyst comprises a maghemite:hematite weight ratio in the range of about 1%:99% to about 70%:30%.
2. The catalyst of claim 1 wherein the weight ratio of maghemite to hematite is about 10%:90%.
3. The catalyst of claim 2 comprising a BET surface area in the range of from about 45 m 2 /g to about 65 m 2 /g.
4. The catalyst of claim 2 comprising a mean pore diameter in the range of from about 75 Å to about 120 Å.
5. The catalyst of claim 2 comprising a mean pore volume in the range of from about 0.20 cc/g to about 0.24 cc/g.
6. The catalyst of claim 2 comprising a mean crystallite size in the range of from about 25 nm to about 29 nm.
7. The catalyst of claim 1 comprising a particulate structure with a particle size distribution in the range of 10 μm-100 μm.
8. The catalyst of claim 1 comprising a BET surface area in the range of from about 45 m 2 /g to about 150 m 2 /g.
9. The catalyst of claim 1 comprising a mean pore diameter in the range of from about 45 Å to about 120 Å.
10. The catalyst of claim 1 comprising a mean pore volume in the range of from about 0.2 cc/g to about 0.6 cc/g.
11. The catalyst of claim 1 comprising a mean crystallite size in the range of from about 15 nm to about 40 nm.
12. The catalyst of claim 1 comprising about 1 part by weight potassium per 100 parts iron.