Asphalt emulsion priming compositions and methods of use
Asphalt emulsion compositions for use in priming a granular surface such as a road bed are provided. The asphalt emulsion comprises asphalt, an amphoteric emulsifier, and water. The asphalt emulsion priming composition may be used on road beds to prepare the road bed for paving. Application of the asphalt emulsion priming composition to a granular surface, such as a road bed, can provide several advantages, including reducing or eliminating dust generated by traffic on the granular surface.
1. An asphalt emulsion composition for use in priming a granular surface comprising:
(a) between about 9% by weight to less than 28.5% by weight asphalt;
(b) between about 0.03% by weight and about 0.9% by weight of an amphoteric emulsifier; and
(c) between about 90.9% by weight and about 71.5% by weight water.
2. The asphalt emulsion composition of claim 1 , wherein the amphoteric emulsifier has one of formula I or formula II:
in which:
R 1 represents an aliphatic, saturated or unsaturated, linear or branched grouping having 6 to 24 carbon atoms;
R 2 is an aliphatic, saturated or unsaturated, linear or branched grouping having 2 to 6 carbon atoms;
R 3 and R 4 , identical or different, represent an aliphatic, saturated or unsaturated, linear or branched grouping, consisting of 1 to 4 carbon atoms;
R 5 is an aliphatic, saturated or unsaturated, linear or branched grouping consisting of 1 to 6 carbon atoms;
Y − is a SO 3 31 or COO 31 group;
Z, identical or different, is a SO 3 31 or COO 31 or OH group.
3. The asphalt emulsion composition of claim 1 , wherein the amphoteric emulsifier is one of cocoamidopropylbetaine or cocoamidohydropropylsultaine.
4. The asphalt emulsion composition of claim 3 , wherein the composition comprises between about 18% to 25% asphalt.
5. A process for producing an asphalt emulsion primer from an asphalt emulsion primer concentrate comprising the steps of:
(a) heating a quantity of asphalt to reduce the viscosity of the asphalt;
(b) mixing an amphoteric emulsifier with water to produce an amphoteric emulsifier solution;
(c) mixing the heated asphalt and the amphoteric emulsifier solution to produce an asphalt-in-water emulsion primer concentrate; and
(d) mixing the asphalt-in-water emulsion primer concentrate with water to produce an asphalt emulsion primer, wherein the resulting asphalt emulsion primer comprises between about 9% by weight to less than 28.5% by weight asphalt.
6. The process of claim 5 , wherein the asphalt emulsion primer comprises between about 9% by weight to less than 28.5% by weight asphalt, between about 0.03% by weight to about 0.9% by weight of an amphoteric emulsifier, and between about 90.9% by weight and about 71.5% by weight water.
7. A process for asphalt priming a granular surface comprising the steps of:
(a) providing an asphalt emulsion primer composition of any one of claims 1 and 2 - 4 ; and
(b) spraying the asphalt emulsion primer composition on a granular surface.
8. The process of claim 5 , further including the step of adding a natural plant oil to the water mixed with the asphalt emulsion primer concentrate.
9. The process of claim 8 , wherein sufficient natural plant oil is added to the water to result in a concentration of the natural plant oil between about 2% by weight and 15% by weight of the total weight of the asphalt emulsion primer composition.
10. The process of claim 9 , wherein the natural plant oil is d-limonene.
11. The process of claim 5 , further including the step of adding sufficient surfactant to the water mixed with the asphalt emulsion primer concentrate to result in a concentration of the surfactant of between about 0.01% by weight and 5% by weight of the total weight of the asphalt emulsion primer composition.
12. The process of claim 7 , wherein the asphalt emulsion primer is sprayed on the granular surface at a rate of about 2 kg asphalt per square meter.