Two component waterborne polyurethane coatings for anti-graffiti application
View Patent ↗Two component (2K) waterborne polyurethane coating compositions which when cured achieve excellent anti-graffiti properties at low VOC level (below 100 g/L) are disclosed. The composition comprises (A) a fluorinated polyol and optionally a non-fluorinated polyol; and (B), a blend of polyisocyanates comprising a hydrophilically modified trimer of hexamethylene diisocyanate (HDT) and a hydrophilic ally modified trimer of isophorone diisocyanate (IPDT). The glass transition temperature of the ambient cured coatings, crosslinked network structure, and fluorine content at the surface enable excellent anti-graffiti properties. The waterborn coatings of the invention have excellent recoatability and exceptional chemical resistance.
1. An anti-graffiti coating composition comprising the reaction product of (A) a polyol blend comprising a fluorinated acrylic polyol and a non-fluorinated acrylic polyol, wherein the fluorinated polyol is a hydroxyl functional styrene acrylic copolymer emulsion and the non-fluorinated polyol is a hydroxyl functional styrene acrylic copolymer emulsion; and (B) a blend of polyisocyanates comprising (i) a hydrophilically modified trimer of hexamethylene diisocyanate (HDT) and (ii) a hydrophilically modified trimer of isophorone diisocyanate (IPDT).
2. The coating composition of claim 1 having a VOC below 100 g/L.
3. The coating composition of claim 1 wherein the fluorinated polyol comprises 1 to 40% by weight of the polyol blend.
4. The coating composition of claim 1 wherein the molar ratio of isocyanate units in the blend of polyisocyanates to hydroxyl units in the polyol blend is about 1 to 3.
5. The coating composition of claim 1 wherein said HDT and IPDT are surfactant based hydrophilic polyisocyanate emulsions in water, auto dispersible in aqueous phase, with at least one surfactant containing an anionic functional group, a countercation and, a polyethylene glycol chain fragment having one or more ethyleneoxy units, wherein the anionic functional group of said surfactant corresponds to the following formula:
wherein: q is zero or 1; p is 1 or 2; m is 0 or 1; the sum: 1+p+2m+q is equal to three or to five; X and X′ are a divalent group; s is an integer chosen between 1 and 30; n is an integer chosen between 1 and 30; E is a phosphorus atom; and R 1 and R 2 are a hydrocarbon radical.
6. The coating composition of claim 1 further comprising a solvent.
7. The coating composition of claim 1 wherein said fluorinated polyol has a glass transition temperature of from 10° C. to 80° C.