Amorphous silica-alumina composition and method of making and using such composition
View Patent ↗Described is a novel amorphous silica-alumina composition having a high ratio of pore volume contained in large pores to pore volume contained in medium to small pores. The amorphous silica-alumina composition also may have the characteristic of a strong aluminum-NMR penta-coordinated peak representing greater than 30% of the total aluminum and a method of making such novel amorphous silica-alumina composition using a pH swing preparation method.
1. A method of making a silica-alumina composition, wherein said method comprises:
(a) combining within a mixing zone water and aluminum sulfate to provide a mixture having a pH in the range of from 1.5 to 6.5;
(b) thereafter, increasing the pH of said mixture to within the range of from 7.5 to 12 by adding sodium silicate to said mixture within said mixing zone; and
(c) recovering a precipitate solid from said mixture in said mixing zone, wherein said precipitate solid comprises highly amorphous silica-alumina containing less than 10 weight percent alumina that is in the crystalline phase and having an A/B ratio exceeding 2.2.
2. A method as recited in claim 1 , further comprising, prior to recovering step (c):
(d) after increasing step (b), lowering the pH of said mixture to within the range of from 1.5 to 6.5 by adding aluminum sulfate to said mixture within said mixing zone; and
(e) thereafter, increasing the pH of said mixture to within the range of from 7.5 to 12 by adding sodium aluminate to said mixture within said mixing zone.
3. A method as recited in claim 2 , further comprising:
(f) after increasing step (e), lowering the pH of said mixture to within the range of from 1.5 to 6.5 by adding aluminum sulfate to said mixture within said mixing zone; and
(e) thereafter, increasing the pH of said mixture to within the range of from 7.5 to 12 by adding sodium silicate to said mixture within said mixing zone.
4. A method of making a silica-alumina composition, wherein said method comprises:
forming within a mixing zone a precipitate solid comprising highly amorphous silica-alumina containing less than 10 weight percent alumina that is in the crystalline phase and having an A/B ratio exceeding 2.2 by:
(a) introducing water into said mixing zone;
(b) introducing aluminum sulfate into said mixing zone so as to provide a mixture comprising water and aluminum sulfate having a pH in the range of from 1.5 to 6.5;
(c) thereafter, introducing sodium aluminate into said mixing zone to thereby increase the pH of said mixture to within the range of from 7.5 to 12;
(d) thereafter, introducing aluminum sulfate into said mixing zone to thereby lower the pH of said mixture to within the range of from 1.5 to 6.5; and
(e) thereafter, introducing sodium silicate into said mixing zone to thereby increase the pH of said mixture to within the range of from 7.5 to 12; and
recovering said precipitate solid from said mixture.
5. A method as recited in claim 4 , further comprising, prior to the recovering step:
(f) after step (e), introducing aluminum sulfate into said mixing zone to thereby lower the pH of said mixture to within the range of from 1.5 to 6.5;
(g) thereafter, introducing sodium aluminate into said mixing zone to thereby increase the pH of said mixture to within the range of from 7.5 to 12;
(h) thereafter, introducing aluminum sulfate into said mixing zone to thereby lower the pH of said mixture to within the range of from 1.5 to 6.5; and
(i) thereafter, introducing sodium silicate into said mixing zone to thereby increase the pH of said mixture to within the range of from 7.5 to 12.
6. A method of making an amorphous silica-alumina composition, wherein said method comprises:
(a) combining water and aluminum sulfate to provide a first mixture having a pH in the range of from 1.5 to 6.5;
(b) adding sodium aluminate to said first mixture to provide a second mixture having a pH in the range of from 7.5 to 12;
(c) adding aluminum sulfate to said second mixture to provide a third mixture having a pH in the range of from 1.5 to 6.5;
(d) adding sodium silicate to said third mixture to provide a forth mixture having a pH in the range of from 7.5 to 12;
(e) adding aluminum sulfate to said forth mixture to provide a fifth mixture having a pH in the range of from 1.5 to 6.5;
(f) adding sodium aluminate to said fifth mixture to provide a sixth mixture having a pH in the range of from 7.5 to 12;
(g) adding aluminum sulfate to said sixth mixture to provide a seventh mixture having a pH in the range of from 1.5 to 6.5;
(h) adding sodium silicate to said seventh mixture to provide an eighth mixture having a pH in the range of from 7.5 to 12; and
(i) recovering a precipitate solid from said eighth mixture, wherein said precipitate solid comprises highly amorphous silica-alumina containing less than 10 weight percent alumina that is in the crystalline phase and having an A/B ratio exceeding 2.2.
7. A method as recited in claim 1 , further comprising: calcining said precipitate solid in the presence of an oxygen-containing atmosphere at a calcination temperature in the range of from 275° C. to 1000° C.
8. A method as recited in claim 2 , further comprising: calcining said precipitate solid in the presence of an oxygen-containing atmosphere at a calcination temperature in the range of from 275° C. to 1000° C.
9. A method as recited in claim 3 , further comprising: calcining said precipitate solid in the presence of an oxygen-containing atmosphere at a calcination temperature in the range of from 275° C. to 1000° C.
10. A method as recited in any one of claims 7 , 8 or 9 , wherein said precipitate solid has a surface area in the range of from 190 m 2 /g to 400 m 2 /g.
11. A method as recited in any one of claims 7 , 8 or 9 , wherein said precipitate solid has a silica content in the range of from 10 to 90 weight percent, with the weight percent being based on the total dry weight of said precipitate solid.
12. A method as recited in claim 4 , further comprising: calcining said precipitate solid in the presence of an oxygen-containing atmosphere at a calcination temperature in the range of from 275° C. to 1000° C.
13. A method as recited in claim 5 , further comprising: calcining said precipitate solid in the presence of an oxygen-containing atmosphere at a calcination temperature in the range of from 275° C. to 1000° C.
14. A method as recited in claim 12 or 13 , wherein said precipitate solid has a surface area in the range of from 190 m 2 /g to 400 m 2 /g.
15. A method as recited in claim 12 or 13 , wherein said precipitate solid has a silica content in the range of from 10 to 90 weight percent, with the weight percent being based on the total dry weight of said precipitate solid.
16. A method as recited in claim 6 , further comprising: calcining said precipitate solid in the presence of an oxygen-containing atmosphere at a calcination temperature in the range of from 275° C. to 1000° C.
17. A method as recited in claim 16 , wherein said precipitate solid has a surface area in the range of from 190 m 2 /g to 400 m 2 /g.
18. A method as recited in claim 17 , wherein said precipitate solid has a silica content in the range of from 10 to 90 weight percent, with the weight percent being based on the total dry weight of said precipitate solid.