Transparent thermoplastic composition with improved electrical conductivity in the melt
View Patent ↗The present invention provides a transparent thermoplastic molding composition made from a transparent blend of a polycarbonate resin with a polyester resin, 0.005 to 2 weight percent, based on the weight of the composition, of a perfluoroalkylsulfonic acid salt of the formula (I): (RA—SO 3 − ) n X n+ (I), wherein R denotes perfluorinated linear or branched carbon chain having 1 to 30 carbon atoms, A denotes a direct bond or an aromatic nucleus, n denotes an integer of 1 or 2, and X denotes a metal element selected from the first or the second column in the Periodic Table of the Elements, and 0 to 5 weight percent, based on the weight of the composition, of a glycerol monostearate. The inventive composition has a total transmittance according to ASTM D-1003 of greater than 84% and an electric resistivity according to ASTM D-257 of less than about 2.5E+06 ohm-m.
1. A transparent thermoplastic molding composition consisting of:
one or more polycarbonates resins;
a transparent polyester resin selected from the group consisting of poly(cyclohexanedimethanol terephthalate), poly(cyclohexanedimethanol-co-ethylene terephthalate), glycol-modified polyethylene terephthalate, poly(1,4-cyclohexanedimethyl-1,4-cyclohexanedicarboxylate) and mixtures therof;
from about 0.005 weight percent to about 2 weight percent, based on the weight of the composition, of a perfluoroalkylsulfonic acid salt of the formula (I):
(RA—SO 3 − ) n X n+ (I),
wherein R denotes perfluorinated linear or branched carbon chain having 1 to 30 carbon atoms, A denotes a direct bond or an aromatic nucleus, n denotes an integer of 1 or 2, and X denotes a metal element selected from the first or the second column in the Periodic Table of the Elements; and
from about 0 weight percent to about 5 weight percent, based on the weight of the composition, of a glycerol monostearate (GMS),
wherein the transparent thermoplastic molding composition has a total transmittance according to ASTM D-1003 of greater than about 84% and an electric resistivity according to ASTM D-257 (at 277° C. after 1000 seconds electrification at 100 volts) of less than about 2.5E+06 ohm-m.
2. The transparent thermoplastic molding composition according to claim 1 , wherein the polycarbonate resin is blended with the polyester resin.
3. The transparent thermoplastic molding composition according to claim 1 , wherein the polycarbonate is selected from the group consisting of homopolycarbonates, copolycarbonates and copolyestercarbonates.
4. The transparent thermoplastic molding composition according to claim 1 , wherein the metal element X is selected from the group consisting of Li, Na, K, Cs, Ca, Mg and Ba.
5. The transparent thermoplastic molding composition according to claim 1 , wherein the perfluoroaalkylsulfonic acid salt is selected from the group consisting of lithium perfluorobutanesulfonate, sodium perfluorobutanesulfonate, potassium perfluorobutanesulfonate, cesium perfluorobutanesulfonate, magnesium perfluorobutanesulfonate, calcium perfluorobutanesulfonate, barium perfluorobutanesulfonate.
6. The transparent thermoplastic molding composition according to claim 1 , wherein the perfluoroalkylsulfonic acid salt comprises from about 0.005 weight percent to about 1 weight percent of the composition.
7. The transparent thermoplastic molding composition according to claim 1 , wherein the glycerol monostearate (GMS) comprises from about 0.03 weight percent to about 1 weight percent of the composition.
8. A process for the production of a transparent thermoplastic molding composition consisting of combining:
one or more polycarbonate resins;
a transparent polyester resin selected from the group consisting of poly(cyclohexanedimethanol terephthalate), poly(cyclohexanedimethanol-co-ethylene terephthalate), glycol-modified polyethylene terephthalate, poly(1,4-cyclogexanedimethyl-1,4-cyclohexanedicarboxylate) and mixtures thereof;
from about 0.005 weight percent to about 2 weight percent, based on the weight of the composition, of a perfluoroalkylsulfonic acid salt of the formula (I):
(RA—SO 3 − ) n X n+ (I),
wherein R denotes perfluorinated linear or branched carbon chain having 1 to 30 carbon atoms, A denotes a direct bond or an aromatic nucleus, n denotes an integer of 1 or 2, and X denotes a metal element selected from the first or the second column in the Periodic Table of the Elements; and
from about 0 weight percent to about 5 weight percent, based on the weight of the composition, of a glycerol monostearate (GMS),
wherein the transparent thermoplastic molding has a total transmittance according to ASTM D-1003 of greater than about 84% and an electric resistivity according to ASTM D-257 at 277° C. after 1000 seconds electrification at 100 volts of less than about 2.5E+06 ohm-m.
9. The process according to claim 8 , wherein the polycarbonate resin is blended with the polyester resin.
10. The process according to claim 8 , wherein the metal element X is selected from the group consisting of Li, Na, K, Cs, Ca, Mg and Ba.
11. The process according to claim 8 , wherein the perfluoroalkylsulfonic acid salt is selected from the group consisting of lithium perfluorobutanesulfonate, sodium perfluorobutanesulfonate, potassium perfluorobutanesulfonate, cesium perfluorobutanesulfonate, magnesium perfluorobutanesulfonate, calcium perfluorobutanesulfonate, barium perfluorobutanesulfonate.
12. The process according to claim 8 , wherein the glycerol monostearate (GMS) comprises from about 0.03 weight percent to about 1 weight percent of the composition.
13. A process for improving the electrical conductivity of a transparent thermoplastic molding composition consisting of combining:
one or more polycarbonate resins;
a transparent polyester resin selected from the group consisting of poly(cyclohexanedimethanol terephthalate), poly(cyclohexanedimethanol-co-ethylene terephthalate), glycol-modified polyethylene terephthalate, poly(1,4-cyclohexanedimethyl-1,4-cyclohexanedicarboxylate) and mixtures thereof;
from about 0.005 weight percent to about 2 weight percent, based on the weight of the composition, of a perfluoroalkylsulfonic acid salt of the formula (I):
(RA—SO 3 − ) n X n+ (I),
wherein R denotes perfluorinated linear or branched carbon chain having 1 to 30 carbon atoms, A denotes a direct bond or an aromatic nucleus, n denotes an integer of 1 or 2, and X denotes a metal element selected from the first or the second column in the Periodic Table of the Elements; and
from about 0 weight percent to about 5 weight percent, based on the weight of the composition, of a glycerol monostearate (GMS),
wherein the transparent thermoplastic molding has a total transmittance according to ASTM D-1003 of greater than about 84% and an electric resistivity according to ASTM D-257 at 277° C. after 1000 seconds electrification at 100 volts of less than about 2.5E+06 ohm-m.
14. The process according to claim 13 , wherein the polycarbonate resin is blended with the polyester resin.
15. The process according to claim 13 , wherein the metal element X is selected from the group consisting of Li, Na, K, Cs, Ca, Mg and Ba.
16. The process according to claim 13 , wherein the perfluoroalkylsulfonic acid salt is selected from the group consisting of lithium perfluorobutanesulfonate, sodium perfluorobutanesulfonate, potassium perfluorobutanesulfonate, cesium perfluorobutanesulfonate, magnesium perfluorobutanesulfonate, calcium perfluorobutanesulfonate, barium perfluorobutanesulfonate.
17. The process according to claim 13 , wherein the glycerol monostearate (GMS) comprises from about 0.03 weight percent to about 1 weight percent of the composition.