Production method of silica aerogel film, anti-reflection coating and optical element
View Patent ↗A method for producing a silica aerogel film by hydrolyzing and polymerizing alkoxysilane in the presence of a base catalyst to prepare an alkaline sol, adding an acid catalyst to the alkaline sol to carry out further hydrolysis and polymerization to prepare a first acidic sol, hydrolyzing and polymerizing alkoxysilane in the presence of an acid catalyst to prepare a second acidic sol, applying a mixture of the first and second acidic sols to a substrate, and drying it.
1. A method for producing a silica aerogel film comprising the steps of hydrolyzing and polymerizing alkoxysilane in the presence of a base catalyst to prepare an alkaline sol, adding an acid catalyst to the alkaline sol to carry out further hydrolysis and polymerization to prepare a first acidic sol, hydrolyzing and polymerizing alkoxysilane in the presence of an acid catalyst to prepare a second acidic sol, mixing said first and second acidic sols, applying the resultant mixed sol to a substrate, and drying it; wherein an average particle size ratio of silica particles in said first acidic sol to silica particles in said second acidic sol in said mixed sol is 18.9-21.4.
2. The method for producing a silica aerogel film according to claim 1 , wherein alkoxysilane for said first acidic sol is a monomer or oligomer of tetraalkoxysilane.
3. The method for producing a silica aerogel film according to claim 1 , wherein alkoxysilane for said second acidic sol is at least one selected from the group consisting of methyltrialkoxysilane, tetraalkoxysilane and their oligomers.
4. The method for producing a silica aerogel film according to claim 1 , wherein said alkaline sol is prepared from a mixture of alkoxysilane, alcohol, water and a base catalyst.
5. The method for producing a silica aerogel film according to claim 1 , wherein said second acidic sol is prepared from a mixture of alkoxysilane, alcohol, water and an acid catalyst.
6. The method for producing a silica aerogel film according to claim 1 , wherein the mass ratio of said first acidic sol to said second acidic sol in said mixed sol is 5-90 on a solid basis.