Non-aqueous electrolyte secondary battery and producing method of electrode
View Patent ↗A non-aqueous electrolyte secondary battery includes a positive electrode, a negative electrode, an electrolyte, and a porous protective film formed on either one or both surfaces of the positive and negative electrodes. The porous protective film includes a binder, fine particles, and a surfactant.
1. A non-aqueous electrolyte secondary battery comprising:
a positive electrode;
a negative electrode;
an electrolyte; and
a porous protective film formed on both surfaces of each of the positive and negative electrodes,
wherein the porous protective film is a single layer that includes a binder, fine particles, and a surfactant selected from the group consisting of sodium dodecylsulfate, lithium dodecylsulfate and sodium hexametaphosphate, the porous protective film having a thickness of 10 μm to 200 μm, and
wherein the surfactant is contained within the porous protective film.
2. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the fine particles includes a metal oxide.
3. The non-aqueous electrolyte secondary battery according to claim 2 , wherein the metal oxide includes at least one member selected from the group consisting of alumina, titania, zirconia, and silica.
4. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the binder includes a fluororesin and a rubber resin.
5. The non-aqueous electrolyte secondary battery according to claim 4 , wherein the fluororesin is polyvinylidene fluoride, and
wherein the rubber resin includes at least one member selected from the group consisting of a styrene-butadiene rubber, an acrylic rubber, and a butadiene rubber.
6. The non-aqueous electrolyte secondary battery according to claim 4 , wherein the fluororesin (A):rubber resin (B) mass ratio (A:B) is 1:9 to 9:1.
7. The non-aqueous electrolyte secondary battery according to claim 1 , wherein a content of the surfactant in a slurry used to form the porous protective film ranges from 0.01 to 3.0 by mass %.
8. The non-aqueous electrolyte secondary battery according to claim 2 , wherein the fine particles are insulating fine particles.
9. The non-aqueous electrolyte secondary battery according to claim 2 , wherein the fine particles have a particle diameter of 0.1 to 50 micrometers.
10. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the porous protective film has a gas permeability of 4 to 600 sec/100 ml.
11. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the fine particles are not aggregated.
12. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the surfactant is lithium dodecylsulfate.
13. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the porous protective film consists essentially of the fine particles, the binder and the surfactant and the fine particles are not aggregated.
14. The non-aqueous electrolyte secondary battery according to claim 1 , wherein the surfactant, the binder, the fine particles and a solvent are mixed together to form a fine particle slurry.
15. The non-aqueous electrolyte secondary battery according to claim 1 , wherein a content of the surfactant in a slurry used to form the porous protective film ranges from 0.05 to 1.0 by mass %.