Fiber including silica and metal oxide
View Patent ↗Techniques for coating a fiber with metal oxide include forming silica in the fiber to fix the metal oxide to the fiber. The coated fiber can be used to facilitate photocatalysis.
1. A method comprising:
providing a solution containing at least one metal oxide precursor to a carbon fiber;
drying the carbon fiber to fix the metal oxide precursor on a surface of the carbon fiber;
providing a polycarbosilane melt to the carbon fiber; and
heating the carbon fiber to obtain a fiber comprising silica and metal oxide, wherein the fiber comprises a silica phase formed in a core of the fiber, and a metal oxide phase formed on the surface of the fiber.
2. The method of claim 1 , wherein the solution containing at least one metal oxide precursor further comprises at least one metal oxide.
3. The method of claim 1 , wherein the metal oxide comprises titanium dioxide.
4. The method of claim 1 , wherein the metal oxide precursor comprises at least one titanium oxide precursor.
5. The method of claim 1 , wherein the metal oxide precursor comprises at least one titanium oxide precursor selected from the group consisting of titanium alkoxide, titanium halide and titanium salt.
6. The method of claim 1 , wherein the metal oxide precursor comprises at least one metal element selected from the group consisting of Zn, Al, Y, Li, B, Na, Ba, Ca, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Zr, Nb, Mo, Ru, Rh, Pd, Ag, W, Pt, Au, Ce and any combination thereof.
7. The method of claim 1 , wherein the solution further contains at least one non-ionic surfactant.
8. The method of claim 7 , wherein the non-ionic surfactant comprises a surfactant selected from the group consisting of polyoxyethylene-type surfactant, polyglycerin-type surfactant, sugar ester-type surfactant, ethylene oxide/propylene oxide block copolymer and any combination thereof.
9. The method of claim 1 , wherein the solution comprises at least one organic solvent selected from the group consisting of water, alcohol and any mixture thereof.
10. The method of claim 1 , wherein drying comprises drying at a temperature of about 0° C. to about 150° C.
11. The method of claim 1 , wherein the polycarbosilane comprises a main chain of the following formula:
wherein R1 and R2 comprise, independently of one another, at least one of H, hydroxy, C 1 -C 4 alkyl, C 1 -C 4 alkoxy or phenyl; and
n comprises an integer between 1 and 30.
12. The method of claim 1 , wherein heating comprises heating at a temperature of about 300° C. to about 1500° C.
13. The method of claim 1 , wherein heating comprises heating under air comprising oxygen gas.
14. The method of claim 1 , wherein a size of the fiber is about 1 mm or less.
15. The method of claim 1 , wherein the solution and the polycarbosilane melt are applied to the carbon fiber at different times.
16. The method of claim 1 , wherein the metal oxide phase on the surface of the fiber is mesoporous.
17. A method comprising:
applying a solution to a carbon fiber, wherein the solution comprises at least one metal oxide;
drying the carbon fiber to fix the metal oxide on a surface of the carbon fiber;
applying a polycarbosilane melt to the carbon fiber; and
heating the carbon fiber to obtain a fiber comprising silica and metal oxide.
18. The method of claim 17 , wherein the carbon fiber has a diameter of about 1 mm or less.
19. The method of claim 18 , wherein the carbon fiber has a specific surface area of about 200 m 2 /g to about 3000 m 2 /g.
20. The method of claim 17 , wherein the fiber comprises a crystalline metal oxide.
21. The method of claim 17 , wherein the heating is performed in the presence of oxygen.
22. The method of claim 17 , wherein the heating is performed at conditions effective to oxidize at least a portion of carbon in the carbon fiber.
23. The method of claim 17 , wherein the metal oxide in the fiber has photocatalytic activity.
24. The method of claim 17 , further comprising disposing the carbon fiber in a fabric.
25. The method of claim 17 , further comprising disposing the fiber in a fabric.
26. The method of claim 17 , wherein the metal oxide is titanium dioxide.
27. The method of claim 17 , wherein the polycarbosilane comprises a main chain of the following formula:
wherein R1 and R2 comprise, independently of one another, at least one of H, hydroxy, C 1 -C 4 alkyl, C 1 -C 4 alkoxy or phenyl; and
n comprises an integer between 1 and 30.