Highly efficient organic light-emitting device using substrate or electrode having nanosized half-spherical convex and method for preparing the same
The present invention provides a transparent substance formed with a plurality of continuous half-spherical convexes having a diameter of 25˜1,000 nm on its first main surface; an organic light-emitting device comprising a substrate, a first electrode, an organic material layer(s) and a second electrode, sequentially, characterized by having a plurality of continuous half-spherical convexes having a diameter of 25˜1,000 nm on the underside of the substrate that does not contact the first electrode and/or the upside of the second electrode that does not contact the organic material layer; and a method for preparing same using a porous aluminum oxide layer forming process.
1. A method for preparing an organic light-emitting device, comprising the steps of:
a) preparing an organic light-emitting device by forming a first electrode, an organic material layer(s) and a second electrode on a substrate;
b) adhering a transparent substance to the underside of the substrate that does not contact the first electrode, the upside of the second electrode that does not contact the organic material layer, or both of them in the organic light-emitting device;
c) before or after the b) step, forming a plurality of continuous half-spherical convexes, having a diameter of 25-1,000 nm, on a first main surface of the transparent substance by a method comprising the steps of:
(i) dipping an aluminum substrate having at least one aluminum surface in an acid solution, and applying an oxidation voltage of 10-400 V to the aluminum substrate so as to form an aluminum oxide layer on one surface of the aluminum substrate, in such a manner that a plurality of continuous recesses are formed on the aluminum oxide layer, and a plurality of continuous recesses having a curvature in identical direction to that of the recesses on the aluminum oxide layer are formed on an interface between the aluminum oxide layer and the aluminum substrate;
(ii) removing the aluminum oxide layer from the aluminum substrate formed with the aluminum oxide layer thereon, thereby forming a plurality of continuous half spherical recesses having a diameter of 25-1,000 nm on one surface of the aluminum substrate; and
(iii) forming a plurality of continuous half-spherical convexes, having a diameter of 25-1,000 nm, on the first main surface of a transparent substance by using the aluminum substrate formed with a plurality of continuous half spherical recesses as a mold.
2. A method for preparing an organic light-emitting device, comprising the steps of:
a) adhering a transparent substance to a substrate;
b) before or after the a) step, forming a plurality of continuous half-spherical convexes, having a diameter of 25-1,000 nm, on a first main surface of the transparent substance by a method comprising the steps of:
(i) dipping an aluminum substrate having at least one aluminum surface in an acid solution, and applying an oxidation voltage of 10-400 V to the aluminum substrate so as to form an aluminum oxide layer on one surface of the aluminum substrate, in such a manner that a plurality of continuous recesses are formed on the aluminum oxide layer, and a plurality of continuous recesses having a curvature in identical direction to that of the recesses on the aluminum oxide layer are formed on an interface between the aluminum oxide layer and the aluminum substrate;
(ii) removing the aluminum oxide layer from the aluminum substrate formed with the aluminum oxide layer thereon, thereby forming a plurality of continuous half spherical recesses having a diameter of 25-1,000 nm on one surface of the aluminum substrate; and forming a plurality of continuous half-spherical convexes, having a diameter of 25-1,000 nm, on the first main surface of a transparent substance by using the aluminum substrate formed with a plurality of continuous half-spherical recesses as a mold;
c) preparing an organic light-emitting device by forming a first electrode, an organic material layer(s) and a second electrode on the upside of the substrate opposite to the side adhering the transparent substance having continuous half spherical con-vexes.
3. The method for preparing an organic light-emitting device according to claim 2 , further comprising:
d) adhering a transparent substance to the upside of the second electrode that does not contact the organic material layer in the organic light-emitting device; and
e) before or after the d) step, forming a plurality of continuous half-spherical convexes, having a diameter of 25-1,000 nm, on the first main surface of the transparent substance on the upside of the second electrode, by a method comprising the steps of:
(i) dipping an aluminum substrate having at least one aluminum surface in an acid solution, and applying an oxidation voltage of 10-400 V to the aluminum substrate so as to form an aluminum oxide layer on one surface of the aluminum substrate, in such a manner that a plurality of continuous recesses are formed on the aluminum oxide layer, and a plurality of continuous recesses having a curvature in identical direction to that of the recesses on the aluminum oxide layer are formed on an interface between the aluminum oxide layer and the aluminum substrate;
(ii) removing the aluminum oxide layer from the aluminum substrate formed with the aluminum oxide layer thereon, thereby forming a plurality of continuous half-spherical recesses having a diameter of 25-1,000 nm, on one surface of the aluminum substrate; and
(iii) forming a plurality of continuous half-spherical convexes, having a diameter of 25-1,000 nm, on the first main surface of a transparent substance by using the aluminum substrate formed with a plurality of continuous half-spherical recesses as a mold.