Thermal embossing of resist reflowed lenses to make aspheric lens master wafer

1. A method of forming a lens master wafer, comprising:

forming a material portion on a substrate;

forming a plurality of isolated sections in the material portion;

reflowing the isolated sections; and

stamping the reflowed sections with a lens stamp to form an aspheric lens shape in each of the reflowed sections.

2. The method of claim 1 , wherein the material portion comprises a polymer.

3. The method of claim 2 , wherein the plurality of isolated sections are formed using a mask and by exposing, developing, and curing the polymer to form the plurality of isolated sections.

4. The method of claim 1 , wherein the reflowed sections have an ellipsoid shape and the aspheric lens shape is formed by stamping the ellipsoid shaped sections with the lens stamp while the substrate and material portion are in a vacuum environment.

5. The method of claim 1 , wherein multiple aspheric lens shapes of differing sizes are formed using multiple lens stamps.

6. The method of claim 1 , further comprising heating the lens stamp while forming the aspheric lens shapes.

7. The method of claim 1 , further comprising heating the substrate while forming the aspheric lens shapes in the polymer.

8. The method of claim 1 , further comprising forming an intermediate negative plating film of the lens master wafer.

9. The method of claim 8 , wherein the intermediate negative plating film comprises nickel.

10. The method of claim 8 , further comprising using the intermediate negative plating film to form lenses.

11. The method of claim 1 , further comprising etching the aspheric lens shapes into the substrate.

12. The method of claim 1 , further comprising:

depositing an ultraviolet curable material onto the lens master wafer; and

curing the ultraviolet curable material using ultraviolet light exposure to form an intermediate negative of the lens master wafer.

13. A method of forming a lens master wafer, comprising:

coating a substrate with a photo-patternable polymer of a predetermined thickness;

coating the polymer with a photoresist;

patterning the photoresist to form etchable areas in the polymer;

etching the polymer using the patterned photoresist to form a plurality of isolated sections;

removing the photoresist;

reflowing the isolated sections to form ellipsoidal shaped sections; and

stamping each of the ellipsoidal shaped sections with a lens stamp to form an aspheric lens shape.

14. The method of claim 13 , further comprising etching the aspheric lens shapes into the substrate.

15. The method of claim 13 , wherein the substrate is heated during the formation of the aspheric lens shapes.

16. The method of claim 13 , wherein the lens stamp is heated during the formation of the aspheric lens shapes.

17. The method of claim 13 , wherein the aspheric lens shapes are formed in a low air pressure environment.

18. The method of claim 13 , wherein the aspheric lens shapes are formed in a vacuum environment.

19. The method of claim 13 , wherein the aspheric lens shapes are formed to be uniform in size.

20. The method of claim 13 , wherein multiple lens stamps of varying sizes are used to form the aspheric lens shapes in varying sizes.

21. The method of claim 13 , wherein the aspheric lens shapes are each cured individually by ultraviolet light exposure during the stamping process.

22. The method of claim 13 , wherein the aspheric lens shapes are cured collectively by heat treatment after the stamping process is complete.

23. The method of claim 13 , wherein the aspheric lens shapes are cured collectively by ultraviolet light exposure after the stamping process is complete.

24. The method of claim 23 , further comprising curing the aspheric lens shapes collectively by heat treatment.

25. The method of claim 13 , further comprising:

depositing an ultraviolet curable material over the aspheric lens shapes; and

exposing the ultraviolet curable material to ultraviolet light to form aspheric lens shapes.