Multicomponent textile fibers, methods for their production, and products made using them
A fiber is produced comprising polymers of differing types which are not admixed during production. The differing polymer types are heated to the point of softening in a vertically-oriented crucible and a fiber comprising the polymers in positions corresponding to their positions in the crucible is drawn from an orifice at the lower end of the crucible.
1. A method of production of a polymer fiber wherein a plurality of differing polymer types are provided as precursor materials and are not admixed during fiber production, whereby the properties of the differing polymer types are preserved in the final fiber, and wherein the properties of the polymers of the fiber vary along its length, comprising the steps of:
providing a vertically-oriented elongated crucible divided by radially- and vertically-extending partitions extending vertically substantially the entire length of the elongated crucible into a plurality of separate vertical compartments for receiving the differing polymer types, each of the compartments communicating at a lower end thereof with an orifice in the lower end of the crucible;
disposing quantities of the differing polymer types in the corresponding compartments in granular form, whereby quantities of different polymer materials are disposed within one or more of the compartments of the crucible one above one another, such that the polymer materials are not admixed with one another in the crucible, and are disposed within said one or more of the compartment so as to differ along the vertical length of the one or more compartments;
heating the crucible to a desired temperature at which each of the differing polymer types are softened to a desired degree;
codrawing a fiber comprising each of the polymer types, being disposed with respect to one another corresponding to the positions of the respective compartments in the crucible, from the orifice; and
reeling the codrawn fiber onto a takeup reel,
whereby a fiber is produced the properties of which vary along its length.
2. The method of claim 1 , comprising the further step of controlling the rate of rotation of the takeup reel with respect to the rate at which the fiber is drawn from the orifice in order to control the final diameter of the fiber.