Soft magnetic iron/cobalt/chromium-based alloy and process for manufacturing it
View Patent ↗A soft magnetic alloy consists essentially of 5 percent by weight≦Co≦30 percent by weight, 1 percent by weight≦Cr≦20 percent by weight, 0.1 percent by weight≦Al≦2 percent by weight, 0 percent by weight≦Si≦1.5 percent by weight, 0.017 percent by weight≦Mn≦0.2 percent by weight, 0.01 percent by weight≦S≦0.05 percent by weight where Mn/S is >1.7, 0 percent by weight≦O≦0.0015 percent by weight, und 0.0003 percent by weight≦Ce≦0.05 percent by weight, 0 percent by weight≦Ca≦0.005 percent by weight and the remainder iron, where 0.117 percent by weight≦(Al+Si+Mn+V+Mo+W+Nb+Ti+Ni)≦5 percent by weight.
1. A soft magnetic alloy consisting essentially of:
an amount of cobalt Co, such that 5 percent by weight≦Co≦30 percent by weight,
an amount of chromium Cr, such that 1 percent by weight≦Cr≦20 percent by weight,
an amount of aluminum Al, such that 0.1 percent by weight≦Al≦2 percent by weight,
optionally, an amount of silicon Si, such that 0 percent by weight≦Si≦1.5 percent by weight,
an amount of manganese Mn, such that 0.017 percent by weight≦Mn≦0.2 percent by weight,
an amount of sulfur S, such that 0.01 percent by weight≦S≦0.05 percent by weight, and wherein where Mn/S>1.7,
optionally, an amount of oxygen O, such that 0 percent by weight≦O≦0.0015 percent by weight,
an amount of cerium Ce, such that 0.001 percent by weight≦Ce≦0.05 percent by weight,
optionally, an amount of calcium Ca, such that 0 percent by weight≦Ce≦0.005 percent by weight,
optionally, amounts of vanadium V, molybdenum Mo, tungsten W, niobium Nb, titanium Ti, and nickel Ni, such that the amounts of Al, Si, and Mn, and any amounts of V, Mo, W, Nb, Ti, and Ni present are such that 0.117 percent by weight≦(Al+Si+Mn+V+Mo+W+Nb+Ti+Ni)≦5 percent by weight,
and the remainder iron,
wherein the alloy has a coercive field strength H c <5.0 A/cm.
2. The soft magnetic alloy in accordance with claim 1 , wherein 0.001 percent by weight≦Ca≦0.005 percent by weight.
3. The soft magnetic alloy in accordance with claim 1 , wherein 0.001 percent by weight≦Ce≦0.02 percent by weight.
4. The soft magnetic alloy in accordance with claim 3 , wherein 0.001 percent by weight≦Ce≦0.005 percent by weight.
5. The soft magnetic alloy in accordance with claim 1 , wherein 8 percent by weight≦Co≦22 percent by weight.
6. The soft magnetic alloy in accordance with claim 5 , wherein 14 percent by weight≦Co≦20 percent by weight.
7. The soft magnetic alloy in accordance with claim 1 , wherein 1.5 percent by weight≦Cr≦3 percent by weight.
8. The soft magnetic alloy in accordance with claim 5 , wherein 6 percent by weight≦Cr≦15 percent by weight.
9. The soft magnetic alloy in accordance with claim 1 , wherein the alloy has a specific electrical resistance ρ el >0.40 μΩm.
10. The soft magnetic alloy in accordance with claim 9 , wherein the alloy has a specific electrical resistance ρ el >0.60 μΩm.
11. The soft magnetic alloy in accordance with claim 1 , wherein the alloy has an apparent yielding point R p0.2 >280 MPa.
12. The soft magnetic alloy in accordance with claim 1 , wherein the alloy has a coercive field strength H c <2.0 A/cm.
13. The soft magnetic alloy in accordance with claim 1 , wherein the alloy has a maximum permeability μ max >1000.
14. A soft magnetic core for an electromagnetic actuator comprising an alloy in accordance with claim 1 .
15. A soft magnetic core for a solenoid valve of an internal combustion engine comprising an alloy in accordance with claim 1 .
16. A soft magnetic core for a fuel injection valve of an internal combustion engine comprising an alloy in accordance with claim 1 .
17. A soft magnetic core for a direct fuel injection valve of a spark ignition engine comprising an alloy in accordance with claim 1 .
18. A soft magnetic core for a direct fuel injection valve of a diesel engine comprising an alloy in accordance with claim 1 .
19. A fuel injection valve of an internal combustion engine comprising a component comprising a soft magnetic alloy in accordance with claim 1 .
20. The fuel injection valve in accordance with claim 19 , wherein the fuel injection valve is a direct fuel injection valve of a spark ignition engine.
21. The fuel injection valve in accordance with claim 19 , wherein the fuel injection valve is a direct fuel injection valve of a diesel engine.
22. A soft magnetic armature for an electric motor comprising an alloy in accordance with claim 1 .
23. A process for manufacturing semi-finished products made of a cobalt/iron alloy in which workpieces are manufactured by:
melting and hot forming a soft magnetic alloy in accordance with claim 1 , and
carrying out a final annealing process on said alloy.
24. The process in accordance with claim 23 , wherein the final annealing is carried out within a temperature range of 700° C. to 1100° C.
25. The process in accordance with claim 24 , wherein the final annealing is carried out within a temperature range of 750° C. to 850° C.
26. The process in accordance with claim 23 , further comprising cold forming the alloy prior to final annealing.
27. The process in accordance with claim 23 , wherein the final annealing process comprises subjecting the alloy to an inert gas, hydrogen or a vacuum.