Method for manufacturing pressure-resistant container liner and liquid crystal resin liner
View Patent ↗A resin composition formed by blending 10 to 25 weight parts of the epoxy modified polystyrene resin (B) to 100 weight parts of the liquid crystal polyester and/or the liquid crystal polyester amide (A) and by melt-kneading the two materials, wherein the resin composition having a melt viscosity of 60 to 4000 Pa·s at a shear rate of 1000/second at a temperature which is 20° C. higher than the melting point and having a melt tension of 20 mN or more at a take-over speed of 15 m/minute, is melt within a temperature range of a melting point to the melting point +40° C., a parison P is formed by extruding it with an extrusion speed equal to or higher than 0.3 kg/minute and lower than 5 kg/minute, a pair of moldings placed so as to sandwich the parison P are closed at a predetermined mold closing pressure, and air is blown into the parison P.
1. A method for manufacturing a pressure-resistant container liner by a blow molding, comprising:
a resin composition melting step of heating a blow molding liquid crystal resin composition within a temperature range from a melting point to the melting point +40° C. to melt the resin composition, the resin composition being produced by blending, melting and kneading (A) 100 weight parts of liquid crystal polyester and/or liquid crystal polyester amide, (B) 10 to 25 weight parts of styrene series copolymer comprising 40 to 97% by weight of one or more kinds of styrenes, 60 to 3% by weight of glycidylester of an α, β-unsaturated acid expressed by a following general formula (1), and 0 to 50% by weight of another vinyl monomer, the styrene series copolymer having an epoxy equivalent of 1700 to 3000 g/eq and a weight average molecular weight of 30000 or more,
where —R′ denotes hydrogen or an alkyl group, and (C) 0 to 100 weight parts of one or more kinds of fibrous, particulate, and plate-like fillers, the resin composition having a melt viscosity of 60 to 4000 Pa·s at a temperature higher than the melting point by 20° C. at a shear rate of 1000/sec and a melt tension of 20 mN or more at a take-over speed of 15 m/min;
a parison forming step of extruding and forming a cylindrical parison with an extrusion speed equal to or higher than 0.3 kg/minute and lower than 5 kg/minute by using the specific resin composition melt in the resin composition melting step;
a mold closing step of placing the parison formed in the parison forming step between a pair of molds forming a cylindrical cavity and of closing the molds; and
a forming step of blowing gas into the parison in the molds closed in the mold closing step to form a liner, wherein: the resin composition in which an increase rate of a melt tension at a twice take-over speed (30 m/minute) to the melt tension at the take-over speed of 15 m/minute is 1.05 or more, is used.
2. A method for manufacturing a pressure-resistant container liner by a blow molding, comprising:
a resin composition melting step of heating a blow molding liquid crystal resin composition within a temperature range from a melting point to the melting point +40° C. to melt the resin composition, the resin composition being produced by blending, melting and kneading (A) 100 weight parts of liquid crystal polyester and/or liquid crystal polyester amide, (B) 10 to 25 weight parts of styrene series copolymer comprising 40 to 97% by weight of one or more kinds of styrenes, 60 to 3% by weight of glycidylester of an α, β-unsaturated acid expressed by a following general formula (1), and 0 to 50% by weight of another vinyl monomer, the styrene series copolymer having an epoxy equivalent of 1700 to 3000 g/eq and a weight average molecular weight of 30000 or more,
where —R′ denotes hydrogen or an alkyl group, and (C) 0 to 100 weight parts of one or more kinds of fibrous, particulate, and plate-like fillers, the resin composition having a melt viscosity of 60 to 4000 Pa·s at a temperature higher than the melting point by 20° C. at a shear rate of 1000/sec and a melt tension of 20 mN or more at a take-over speed of 15 m/min;
a parison forming step of extruding and forming a cylindrical parison with a shear rate equal to or higher than 50/second and lower than 1000/second by using the specific resin composition melt in the resin composition melting step;
a mold closing step of placing the parison formed in the parison forming step between a pair of molds forming a cylindrical cavity and of closing the molds; and
a forming step of blowing gas into the parison in the molds closed in the mold closing step to form a liner, wherein: the resin composition in which an increase rate of a melt tension at a twice take-over speed (30 m/minute) to the melt tension at the take-over speed of 15 m/minute is 1.05 or more, is used.
3. The method for manufacturing the pressure-resistant container liner as claimed in claim 1 or 2 , wherein:
when the mold closing step is performed, a value obtained by dividing a mold closing pressure by a thickness of a pinch-off section is of 3.5 MPa/cm or more.
4. The method for manufacturing the pressure-resistant container liner as claimed in claim 1 or 2 , wherein:
two-stage pinch sections are provided in the molds and a space is formed between the two-stage pinch sections when the molds are closed in the mold closing step.
5. A liquid crystal resin liner manufactured by the method for manufacturing the pressure-resistant container liner as claimed in claim 1 or 2 , wherein a tensile breaking elongation in all directions of a trunk section is 2% or more and a tensile breaking elongation in a pinch-off section is 1% or more.
6. The liquid crystal resin liner as claimed in claim 5 , wherein:
the pinch-off section has a thickness of 2 mm or more.