Heat-resistant Sn-plated Cu-Zn alloy strip with suppressed whiskering
View Patent ↗In an Sn-plated strip in which a copper alloy containing 15 to 40 mass % of Zn in terms of an average concentration is used as an alloy strip and the layers of an Sn phase, an Sn—Cu alloy phase and an Ni phase constitute a plating film from the surface to the alloy strip, the Zn concentration of the surface of the Sn phase is adjusted to a range of 0.1 to 5.0 mass %. The alloy may further contain 0.005 to 3.0 mass % in total of an arbitrary constituent selected from Sn, Ag, Pb, Fe, Ni, Mn, Si, Al and Ti. Moreover, the alloy may be a copper base alloy containing 15 to 40 mass % of Zn, 8 to 20 mass % of Ni, 0 to 0.5 mass % of Mn and a balance of Cu and unavoidable impurities, and may further contain 0.005 to 10 mass % in total of the above arbitrary constituent. There is provided a Cu/Ni double layer base reflowed Sn-plated Cu—Zn alloy strip in which generation of whiskers is suppressed.
1. A Sn-plated Cu-Zn alloy strip in which generation of whiskers is suppressed, wherein a copper alloy containing 15 to 40 mass % of Zn in terms of an average concentration is used as an alloy strip, layers of an Sn phase, an Sn—Cu alloy phase and an Ni phase constitute a plating film in that order from an outer surface of the plating film to the alloy strip, and the Zn concentration of the outer surface of the Sn phase is in a range of 0.1 to 5.0 mass % and wherein the layers are formed by:
Ni plating in a thickness of 0.1 μm or more, and then performing Cu plating in a thickness of 0.1 μm or more (provided that the total of the Ni plating thickness and the Cu slating thickness is in a range of 0.3 to 1.0 μm);
Sn plating in a thickness of 0.3 to 1.0 μm; and
a reflow treatment for heating time t (seconds) and at a heating temperature T (°C.) represented by the following three equations:
5≦t≦23,
350≦T≦600, and
500≦( T +14 t )≦670.
2. The Sn-plated Cu—Zn alloy strip according to claim 1 , wherein a copper base alloy containing 15 to 40 mass % of Zn and a balance of Cu and unavoidable impurities is used as said copper alloy.
3. The Sn-plated Cu—Zn alloy strip according to claim 2 , wherein said copper alloy further contains 0.005 to 10 mass % in total of at least one element selected from the group consisting of Sn, Ag, Pb, Fe, Ni, Mn, Si, Al and Ti.
4. The Sn-plated Cu—Zn alloy strip according to claim 1 , wherein a copper base alloy containing 15 to 40 mass % of Zn, 8 to 20 mass % of Ni, 0 to 0.5 mass % of Mn and a balance of Cu and unavoidable impurities is used as said copper alloy.
5. The Sn-plated Cu—Zn alloy strip according to claim 4 , wherein said copper alloy further contains 0.005 to 10 mass % in total of at least one element selected from the group consisting of Sn, Ag, Pb, Fe, Si, Al and Ti.
6. A manufacturing method of an Sn-plated strip in which generation of whiskers is suppressed, comprising successively subjecting a copper alloy containing 15 to 40 mass % of Zn in terms of an average concentration to the following steps:
a. a step of adjusting the Zn concentration at a position of 0.1 82 m from the surface of an alloy strip to a range of 10 to 40 mass % by surface polishing;
b. a step of performing Ni plating in a thickness of 0.1 μm or more, and then performing Cu plating in a thickness of 0.1 μm or more (provided that the total of the Ni plating thickness and the Cu plating thickness is in a range of 0.3 to 1.0 μm);
c. a step of performing Sn plating in a thickness of 0.3 to 1.0 μm; and
d. a step of performing a reflow treatment for heating time t (seconds) and at a heating temperature T (°C.) represented by the following three equations:
5≦t≦23,
350≦T≦600, and
500≦( T +14 t )≦670.
wherein the Zn concentration of the surface of the Sn phase after step d. is in a range of 0.1 to 5.0 mass %.