Ferrite material and method for producing ferrite material

1. A ferrite material having a composition formula of (1-x-y-z)(Li 0.5 Fe 0.5 )O.xZnO.y(Mn, Fe) 2 O 3 .zCuO, wherein x, y, z, and a satisfy 0.175≦x≦0.29; 0.475≦y≦0.51; 0.07≦z≦0.22; and 0.02≦a≦0.055 in a case of a=Mn/(Mn+Fe);

wherein at least one of Co oxide, Co hydroxide and Co carbonate in an amount of 1 wt. % or less on the basis of CoO is contained in 100 wt. % of the ferrite material.

2. The ferrite material according to claim 1 , wherein a normalized impedance Z N at 30 MHz is 40000 Ω/m or more and a normalized impedance Z N at 100 MHz is 60000 Ω/m or more.

3. The ferrite material according to claim 1 , wherein a specific resistance is 10 6 Ωm or more.

4. The ferrite material according to claim 1 , wherein a change rate of an initial magnetic permeability is within ±10% when a pressure is applied at a pressure of 30 MPa.

5. The ferrite material according to claim 1 , wherein the ferrite material is a ferrite sintered body obtained by successively carrying out the respective treatments of calcinating, grinding, molding and firing for raw material powders.

6. The ferrite material according to claim 1 , wherein the ferrite material is ferrite powders obtained by firing raw material powders.

7. The ferrite material according to claim 1 , wherein the ferrite material is ferrite powders obtained by successively carrying out the respective treatments of calcinating, grinding, and firing for raw material powders.

8. The ferrite material according to claim 1 , wherein the ferrite material is ferrite powders obtained by successively carrying out the respective treatments of calcinating, grinding, molding, firing, and grinding for raw material powders.

9. A method for producing a ferrite material, comprising the steps of:

preparing raw material powders having a composition formula of (1-x-y-z)(Li 0.5 Fe 0.5 )O.xZnO.y(Mn, Fe) 2 O 3 .zCuO, wherein x, y, z, and a satisfy 0.175≦x≦0.29; 0.475≦y≦0.51; 0.07≦z≦0.22; and 0.02≦a≦0.055 in a case of a=Mn/(Mn+Fe);

obtaining calcinated powders by calcinating the raw material powders;

obtaining grinded powders by grinding the calcinated powders;

obtaining a molded body by molding the grinded powders;

obtaining a ferrite sintered body by firing the molded body; and

adding at least one of Co oxide, Co hydroxide and Co carbonate, in an amount of 1 wt. % or less on the basis of CoO relative to 100 wt. % of an object material to be added, before the firing is carried out.

10. A method for producing a ferrite material, comprising the steps of:

preparing raw material powders having a composition formula of (1-x-y-z)(Li 0.5 Fe 0.5 )O.xZnO.y(Mn, Fe) 2 O 3 .zCuO, wherein x, y, z, and a satisfy 0.175≦x≦0.29; 0.475≦y≦0.51; 0.07≦z≦0.22; and 0.02≦a≦0.055 in a case of a=Mn/(Mn+Fe);

obtaining ferrite powders by firing the raw material powders; and

adding at least one of Co oxide, Co hydroxide, and Co carbonate in an amount of 1 wt. % or less on the basis of CoO relative to 100 wt. % of an object material to be added, before the firing is carried out.

11. The method for producing a ferrite material according to claim 10 , wherein the temperature at the time of firing the raw material powders is 800° C. to 1050° C.

12. A method for producing a ferrite material, comprising the steps of:

preparing raw material powders having a composition formula of (1-x-y-z)(Li 0.5 Fe 0.5 )O.xZnO.y(Mn, Fe) 2 O 3 .zCuO, wherein x, y, z, and a satisfy 0.175≦x≦0.29; 0.475≦y≦0.51; 0.07≦z≦0.22; and 0.02≦a≦0.055 in a case of a=Mn/(Mn+Fe);

obtaining calcinated powders by calcinating the raw material powders;

obtaining grinded powders by grinding the calcinated powders;

obtaining ferrite powders by firing the grinded powders; and

adding at least one of Co oxide, Co hydroxide and Co carbonate in an amount of 1 wt. % or less on the basis of CoO relative to 100 wt. % of an object material to be added, before the firing is carried out.

13. A method for producing a ferrite material, comprising the steps of:

preparing raw material powders having a composition formula of (1-x-y-z)(Li 0.5 Fe 0.5 )O.xZnO.y(Mn, Fe) 2 O 3 .zCuO, wherein x, y, z, and a satisfy 0.175≦x≦5 0.29; 0.475≦y≦0.51; 0.07≦z≦0.22; and 0.02≦a≦0.055 in a case of a=Mn/(Mn+Fe);

obtaining calcinated powders by calcinating the raw material powders;

obtaining grinded powders by grinding the calcinated powders;

obtaining a molded body by molding the grinded powders;

obtaining a sintered body by firing the molded body; and

obtaining ferrite powders by grinding the sintered body.

14. The method for producing a ferrite material according to claim 13 , further comprising the step of:

adding at least one of Co oxide, Co hydroxide, and Co carbonate in an amount of 1 wt. % or less on the basis of CoO relative to 100 wt. % of an object material to be added, before the firing is carried out.