Method of manufacturing a glass substrate, glass substrate manufactured by the method, and magnetic recording medium using the glass substrate
View Patent ↗An object of the present invention is to provide a method of manufacturing a glass substrate containing alkali metals. A glass substrate manufactured by the method exhibits excellent performances including durability by virtue of suppressing elution of alkali metals. A method comprises a step of immersing a glass material in an aqueous solution containing a formate to suppress elution of component of the glass material.
1. A method of manufacturing a glass substrate, comprising the steps of:
a. providing a glass substrate comprised of an alkali metal oxide glass containing an oxide of at least one alkali metal; and
b. immersing the glass substrate in an aqueous solution containing potassium formate dissolved in water and present in an amount ranging from an amount effective to raise an ion exchange rate between hydronium ions (H3O+) generated from the water and alkali metal in the glass substrate sufficient to achieve reformation of a surface of the glass substrate up to 77.7 wt %,
wherein immersing takes place at a process temperature ranging from 120° C. to 210° C., and for a process time ranging from 1 to 270 minutes so that subsequent elution of alkali metal from the glass substrate is suppressed.
2. The method of manufacturing a glass substrate according to claim 1 , wherein the aqueous solution has a temperature of at most 140° C. during immersing.
3. The method of manufacturing a glass substrate according to claim 1 , further comprising removing residual potassium formate by immersing the glass substrate in warm water having a temperature of at least 70° C. after the step of immersing the glass substrate in the aqueous solution containing potassium formate dissolved in water.
4. The method of manufacturing a glass substrate according to claim 3 , wherein immersion in the warm water continues for an immersion time of at least 10 min.
5. A glass substrate comprised of an alkali metal oxide glass which has a reformed surface due to having been immersed in an aqueous solution containing potassium formate dissolved in water, and which is manufactured by the method of manufacturing a glass substrate as defined by claim 1 .
6. A magnetic recording medium, comprising the glass substrate as defined by claim 5 which has a reformed surface due to having been immersed in an aqueous solution containing potassium formate dissolved in water.
7. The method of manufacturing a glass substrate according to claim 1 , wherein the process temperature ranges from 130° C. to 140° C., and wherein the process time ranges from 60 to 270 minutes.
8. The method of manufacturing a glass substrate according to claim 1 , wherein the aqueous solution has a temperature of at most 200° C. during immersing.
9. The method of manufacturing a glass substrate according to claim 1 , wherein the process temperature ranges from 130° C. to 150° C., and wherein the process time ranges from 15 to 270 minutes.