Dispersible and conductive nano graphene platelets

1. A dispersible and electrically conductive nano graphene platelet (NGP) material comprising at least a single-layer or multiple-layer graphene sheet, wherein said NGP material has an oxygen content no greater than 25% by weight and no less than 5% by weight, wherein said nano graphene platelet material is obtained from a process comprising: (a) preparing a pristine NGP material from a graphitic material; and (b) subjecting said pristine NGP material to an oxidation treatment to obtain said dispersible and conductive NGP material and wherein said graphitic material is selected from the group consisting of natural graphite, artificial graphite, graphite oxide, graphite fluoride, graphite fiber, carbon fiber, carbon nano-fiber, carbon nano-tube, mesophase carbon micro-bead (MCMB) or carbonaceous micro-sphere (CMS), soft carbon, hard carbon, and combinations thereof.

2. The material as set forth in claim 1 wherein said NGP has an oxygen content in the range of approximately 5% to 20% by weight inclusive.

3. The material as set forth in claim 1 wherein said nano graphene platelet material, when formed into a thin film with a thickness no greater than 100 nm, exhibits an electrical conductivity of at least 10 S/cm.

4. The material as set forth in claim 1 wherein said nano graphene platelet material, when formed into a thin film with a thickness no greater than 100 nm, exhibits an electrical conductivity of at least 100 S/cm.

5. The material as set forth in claim 1 wherein said nano graphene platelet material, when formed into a thin film with a thickness no greater than 100 nm, exhibits an electrical conductivity of at least 1,000 S/cm.

6. The material as set forth in claim 1 wherein said nano graphene material has a specific surface area of approximately from 300 m 2 /g to 2,600 m 2 /g.

7. The material as set forth in claim 1 wherein said nano graphene platelet material comprises single-layer graphene.

8. The material as set forth in claim 1 wherein said oxidation treatment comprises subjecting said pristine NGP material to an oxidizing agent selected from ozone, sulfonic vapor (SO 3 ), an oxygen-containing gas, hydrogen peroxide vapor, nitric acid vapor, or a combination thereof.

9. The material as set forth in claim 1 wherein said pristine NGP material is obtained from a process comprising a procedure selected from:

a. intercalating said graphitic material with a non-oxidizing agent, followed by a thermal or chemical exfoliation treatment in a non-oxidizing environment;

b. subjecting said graphitic material to a supercritical fluid environment for inter-graphene layer penetration and exfoliation;

c. dispersing said graphitic material in a powder form to an aqueous solution containing a surfactant or dispersing agent to obtain a suspension; and subjecting said suspension to direct ultrasonication;

or a combination thereof.

10. The material as set forth in claim 1 , further comprising a functional group selected from alkyl or aryl silane, alkyl or aralkyl group, hydroxyl group, carboxyl group, amine group, aldehydic group, quinoidal, fluorocarbon, or a combination thereof.

11. A dispersible and electrically conductive nano graphene platelet (NGP) material comprising at least a single-layer or multiple-layer graphene sheet, wherein said NGP material has an oxygen content no greater than 25% by weight and no less than 5% by weight and said NGP further comprises a functional group attached to a surface or edge of the nano graphene platelet material, wherein said functional group is selected from alkyl or aryl silane, alkyl or aralkyl group, hydroxyl group, carboxyl group, amine group, aldehydic group, quinoidal, fluorocarbon, or a combination thereof.

12. A dispersible and electrically conductive nano graphene platelet (NGP) material comprising at least a single-layer or multiple-layer graphene sheet, wherein said NGP material has an oxygen content no greater than 25% by weight and no less than 5% by weight, wherein said NGP material is obtained from a process comprising: (a) preparing a graphite intercalation compound (GIC) or graphite oxide (GO) from a laminar graphite material; (b) exposing said GIC or GO to a first temperature for a first period of time to obtain exfoliated graphite; and (c) exposing said exfoliated graphite to a second temperature in a protective atmosphere for a second period of time, and wherein said nano graphene platelet material, when formed into a thin film with a thickness no greater than 100 nm, exhibits an electrical conductivity of at least 100 S/cm.

13. The material as defined in claim 12 , wherein said protective atmosphere comprises an inert gas, nitrogen, hydrogen, a combination thereof, or vacuum.

14. The material as defined in claim 12 , wherein said first temperature is between approximately 200° C. and 1,500° C.

15. The material as set forth in claim 12 wherein said first temperature is between approximately 800° C. and 1,300° C.

16. The material as set forth in claim 12 wherein said second temperature is between approximately 800° C. and 1,500° C.

17. The material as set forth in claim 12 wherein said second temperature is at least 1,000° C.

18. The material as set forth in claim 12 wherein said second temperature is at least 1,200° C. and the second period of time is at least 2 minutes.